Abstract:The extent of irreversible deactivation of Pt towards hydrogen oxidation reaction (HOR) due to sulfur adsorption and subsequent electrochemical oxidation is quantified in a functional PEM fuel cell. At 70 °C, sequential hydrogen sulfide (H2S) exposure and electrochemical oxidation experiments indicate that as much as 6% of total Pt sites are deactivated per monolayer sulfur adsorption at open circuit potential of a PEM fuel cell followed by its removal. The extent of such deactivation is much higher when the electrode is exposed to H2S when the fuel cell is operating at a finite load, and is dependent on the local overpotential and the duration of exposure. Regardless of this deactivation, the H2/O2 polarization curves obtained on post-recovery electrodes do not show performance losses suggesting that such performance curves alone cannot be used to assess the extent of recovery due to sulfur poisoning. A concise mechanism for the adsorption and electro-oxidation of H2S on Pt anode is presented. H2S dissociatively adsorbs onto Pt as two different sulfur species and at intermediate oxidation potentials, undergoes electro-oxidation to sulfur and then to sulfur dioxide (SO2). This mechanism is validated by charge balances between hydrogen desorption and sulfur electro-oxidation on Pt. The ignition potential for sulfur oxidation decreases with increase in temperature, which coupled with faster electro-oxidation kinetics result in the easier removal of adsorbed sulfur at higher temperatures. Furthermore, the adsorption potential is found to influence sulfur coverage of an electrode exposed to H2S. As an implication, the local potential of a PEM fuel cell anode exposed to H2S contaminated fuel should be kept below the equilibrium potential for sulfur oxidation to prevent irreversible loss of Pt sites.

Sulfur Poisoning on SOFC Ni Anodes: Thermodynamic Analyses within Local Equilibrium Anode Reaction Model

Effective Anodic Sulfide Removal Catalyzed by Single Nickel Atoms on Nitrogen-Doped Graphene with Stainless Steel Substrate

Insight into the Effective Electrocatalytic Sulfide Removal from Aqueous Solutions Using the Surface Oxidized Stainless-Steel Anode and Its Desulfurization Mechanism

Studying the Sulfur Poisoning Mechanism of Solid Oxide Fuel Cells by Means of Patterned Nickel/Yttrium-Stabilized Zirconia Electrodes

Sulfur Poisoning of SOFC Cathodes

Activation of H(2) oxidation at sulphur-exposed Ni surfaces under low temperature SOFC conditions

Sulfur-poisoned Ni-based solid oxide fuel cell anode characterization by varying water content

Investigations on sulfur poisoning mechanisms of a solid oxide fuel cell with niobium-doped ferrate perovskite anode

Hydrogen sulfide poisoning in solid oxide fuel cells under accelerated testing conditions

Analysis of Thermal Stress in a Solid Oxide Fuel Cell Due to the Sulfur Poisoning Interface of the Electrolyte and Cathode

Thermal Stress Analysis of Sulfur Deactivated Solid Oxide Fuel Cells

Synergistic effects of sulfur poisoning and gas diffusion on polarization loss in anodes of solid oxide fuel cells

The Mechanism of H[sub 2]S Poisoning Ni/YSZ Electrode Studied by Impedance Spectroscopy

Sulfur poisoning of La(Ni0.6Fe0.4)O3 cathode material for solid oxide fuel cells

Sulfur Tolerance Improvement of Ni-YSZ Anode by Alkaline Earth Metal Oxide BaO for Solid Oxide Fuel Cells

Performance and Sulfur Poisoning of Ni/CeO2 Impregnated La0.75Sr0.25Cr0.5Mn0.5O3−δ Anode in Solid Oxide Fuel Cells

Analysis of Sulfur Poisoning on a PEM Fuel Cell Electrode

Anode Degradation in SOFC: Fuel Impurity Effects on Nickel Component

Sulfur Poisoning and the Regeneration of the Solid Oxide Fuel Cell with Metal Catalyst-Impregnated La0.75Sr0.25Cr0.5Mn0.5O3-δ Anode

A review of sulfur poisoning of solid oxide fuel cell cathode materials for solid oxide fuel cells

Rational Design of Perovskite-based Anode with Decent Activity for Hydrogen Electro-oxidation and Beneficial Effect of Sulfur for Promoting Power Generation in Solid Oxide Fuel Cells.