Effects of doping La_2O_3 on crystallization and mechanical properties of lithium disilicate glass-ceramics
LUO Zhi-wei,LU An-xian,HAN Li-guo
DOI: https://doi.org/10.3321/j.issn:1004-0609.2009.11.021
2009-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The SiO2-Li2O-K2O-B2O3 glasses doping La2O3 were prepared by traditional melting quenching method,using P2O5 and ZrO2 as complex nucleating agent and Sb2O3 as clarifying agent.The effects of La2O3 content on the crystallization behavior,the crystalline phase and the mechanical properties of the glass-ceramics were investigated by using of DSC,XRD,SEM and mechanical property tester.The results show that,the change of La2O3 content mainly influences the exothermic peak temperature rather than the second exothermic peak temperature.When La2O3 content is lower than 0.40%(mole fraction),the doping content of La2O3 does not change the main crystal phase type in the glass-ceramics.However,when the La2O3 content increases to 0.80%,the La2O3 directly involves in the lattice construction of LaPO4 micro-crystals.At the same time,La2O3 doping increases the precipitation temperature of Li2Si2O5 phase.When the La2O3 content is 0.40%,the glass-ceramics has the highest bending strength and elastic modulus,which are 328 MPa and 143 GPa,respectively.When La2O3 content is lower than 0.40% and higher than 1.20%,the fracture toughness of the glass-ceramics changes slightly with increasing La2O3 content.However,when La2O3 content is 0.40%-1.20%,the fracture toughness increases obviously with increasing La2O3 content,the biggest fracture toughness of the glass-ceramics reaches up to 3.34 MPa.m1/2.