Abstract:An effort to develop smaller, well-dispersed catalytic materials electrochemically on high-surface-area carbon supports is required for improved fuel cell performance. A high-surface-area carbon material of interest is carbon nano-onions (CNOs), also known as multilayer fullerenes. The most convenient synthesis method for CNOs is annealing nanodiamond particles, thus retaining the size of the precursors and providing the possibility to prepare very small nanocatalysts using electrochemical techniques. In terms of pure metal catalysts, platinum is the most common catalyst used in fuel cells. The combination of Pt nanoparticles with CNOs could lead to new catalytic nanomaterials. In this work, this was accomplished by using a rotating disk-slurry electrode (RoDSE) technique. The Pt/CNO catalysts were prepared from slurries that contained functionalized CNOs and K(2)PtCl(6) as the platinum precursor in aqueous 0.1 M H(2)SO(4) solution. X-ray photoelectron spectroscopy results showed that 37% of the Pt on the CNOs is metallic Pt whereas 63% had higher binding energies, which is evidence of higher oxidation states or the presence of Pt atoms and clusters on CNOs. However, aberration-corrected scanning transmission electron microscopy of the Pt/CNOs confirmed the presence of Pt atoms and clusters on CNOs. Thermal gravimetric analysis showed the excellent thermal stability of the Pt/CNOs and a lower onset potential for the electrochemical oxidation of methanol compared to that of commercial Pt/Vulcan catalyst material. The computational method confirmed the Pt atoms' location at CNOs surface sites. Geometric parameters for distances between Pt atoms in the 3Pt/CNOs molecular system from our theoretical calculations are in agreement with the respective parameters obtained experimentally. The combination of CNO with RoDSE presents a new highly dispersed catalyst nanomaterial.

High dispersion and electrocatalytic properties of platinum nanoparticles on surface-oxidized single-walled carbon nanotubes

Preparation, Structure and Electrochemical Hydrogenation of Carbon Nanotubes Supported Platinum Catalysts

Pt Nanoclusters Electrodeposited on Single-Walled Carbon Nanotubes for Electrochemical Catalysis

Platinum Single-Atom and Cluster Anchored on Functionalized MWCNTs with Ultrahigh Mass Efficiency for Electrocatalytic Hydrogen Evolution

Porous Platinum Nanotubes for Oxygen Reduction and Methanol Oxidation Reactions

Effect of Platinum Nanoparticle Loading on Oxygen Reduction at a Pt Nanocluster-Activated Microporous–Mesoporous Carbon Support

Single‐atom Pt on carbon nanotubes for selective electrocatalysis

Synthesis, Purification, and Electrocatalytic Activity of Platinum Nanocatalyst with Globular Dendritic Structure

Cu-template-dependent synthesis of PtCu nanotubes for oxygen reduction reactions

Electro-catalytic Oxidation of CO on Pt Catalyst Supported on Carbon Nanotubes Pretreated with Oxidative Acids

Platinum-Decorated Au Porous Nanotubes As Highly Efficient Catalysts For Formic Acid Electro-Oxidation

Enhanced Electrocatalytic Activity And Stability Toward The Oxygen Reduction Reaction With Unprotected Pt Nanoclusters

Platinum electrodeposition on unsupported carbon nano-onions

Phase Segregated Pt–SnO 2 /C Nanohybrids for Highly Efficient Oxygen Reduction Electrocatalysis

Catalytic Performance of Pt Nanowire Arrays for Oxygen Reduction

Enhanced Stability of Immobilized Platinum Nanoparticles through Nitrogen Heteroatoms on Doped Carbon Supports

Sub-1 Nm Pt Nanoclusters on N and P Co-Doped Carbon Nanotubes for the Electrocatalytic Hydrogen Evolution Reaction

Remarkable Support Effect of SWNTs in Pt Catalyst for Methanol Electrooxidation

Ion-exchange-assisted synthesis of Pt-VC nanoparticles loaded on graphitized carbon: a high-performance nanocomposite electrocatalyst for oxygen-reduction reactions.

A kind of electro-catalyst with high efficiency for hydrogen evolution reaction: Platinum particles dispersed on multi-walled carbon nanotubes

Electrocatalysts: Facile Construction of Pt–Co/CNx Nanotube Electrocatalysts and Their Application to the Oxygen Reduction Reaction (adv. Mater. 48/2009)