Abstract:Nanostructured Pt-on-Au electrocatalysts (coded as Pt-m<boolean AND>Au, 717 shows the atomic Pt/Au ratio) were prepared by deposition of Pt on colloidal Au particles ((10.0 +/- 1.2) nm) and then employed for electro-oxidation of formic acid at concentrations of 0.2-3.2 mol/L by cyclic voltammetry. The electro-oxidation behavior of formic acid was greatly influenced by the morphology and dispersion of Pt deposits on the Au nanoparticles. The electro-oxidation of formic acid occurred mainly in the high potential range (0.6-1.0 V vs SCE) when the Pt existed as a shell fully covering the Au particles in the Pt-m <boolean AND>Au/C catalysts (m > 0.2), which is similar to the electro-catalysis of a Pt/C catalyst. When the state of Pt deposits was varied from a mono-atomic Pt shell (m approximate to 0.2) to very small flocks of Pt clusters or two-dimensional rafts ( m < 0.2) on the same Au particles, dramatic enhancement in the oxidation current of formic acid was observed in the low potential range (- 0.2-0.6 V vs SCE). The mass-specific activity of Pt at peak potential (0.38 V) in a Pt-0.05<boolean AND>Au/C catalyst with a 100 % Pt dispersion (EAS= 236 m(2)/g.Pt) was as high as about 40 times that of traditional Pt/C catalysts with about 30% Pt dispersion (EAS = 74 m(2)/g.pt). These results demonstrate that the catalytic activity of Pt <boolean AND>Au/C catalysts for formic acid electro-oxidation could be dramatically enhanced by decreasing the size of Pt entities or increasing the Pt dispersion on Au particles. On varying the concentration of formic acid, we observed distinct volcano curves by correlating the electro-oxidation current with the concentration of formic acid for both Pt-m<boolean AND>Au/C and Pt/C catalysts. Therefore, the determination of an appropriate concentration window for formic acid can be a key factor to the power densities of direct formic acid fuel cells using Pt-based electrocatalysts.

Platinum-Decorated Au Porous Nanotubes As Highly Efficient Catalysts For Formic Acid Electro-Oxidation

Ultralow‐Platinum‐Loading High‐Performance Nanoporous Electrocatalysts with Nanoengineered Surface Structures

Mesoporous AgPdPt Nanotubes As Electrocatalysts for the Oxygen Reduction Reaction

Electro-oxidation of Formic Acid on Nanostructured Pt-on-Au(Pt^ Au) Electrocatalysts

Electro-oxidation of formic acid on nanostructured Pt-on-Au (Pt boolean AND Au) electrocatalysts

Porous Platinum Nanotubes for Oxygen Reduction and Methanol Oxidation Reactions

Comparative study on formic acid electro-oxidation by shape-controlled platinum@palladium nanocrystals

Carbon Supported Pd-Pt-Ag Hollow Nanocatalysts for Efficient Electrooxidation of Formic Acid

Ultralow Pt loading nanoporous Au-Cu-Pt thin film as highly active and durable catalyst for formic acid oxidation

The trimetallic AuAgPt nanowires for light-enhanced formic acid electrolysis

Porous palladium phosphide nanotubes for formic acid electrooxidation

Carbon-Supported Pd−Pt Nanoalloy with Low Pt Content and Superior Catalysis for Formic Acid Electro-oxidation

High Surface Area Nanoporous Platinum: Facile Fabrication and Electrocatalytic Activity

Synthesis of Ultrathin and Composition-Tunable PdPt Porous Nanowires with Enhanced Electrocatalytic Performance

Unveiling the Influence of Inherent Parameters of AgPt and AgPtAu Octahedra Upon Formic Acid Electrooxidation

Monolayer Supertubes of Carbon-Armored Platinum Nanocrystals Enabling Robust Oxygen Reduction Electrocatalysis

Design and Fabrication of the High Efficient Platinum-Nanoporous Gold Catalysts

Structural Design and Facile Synthesis of a Highly Efficient Catalyst for Formic Acid Electrooxidation.

High dispersion and electrocatalytic properties of platinum nanoparticles on surface-oxidized single-walled carbon nanotubes

Cu5Pt Dodecahedra with Low-Pt Content: Facile Synthesis and Outstanding Formic Acid Electrooxidation

Pd Nanoparticles Supported on Carbon-Modified Rutile TiO2 As a Highly Efficient Catalyst for Formic Acid Electrooxidation