PtCu nanoalloy loaded on sulfur-doped porous g-C 3 N 4 for electrocatalytic hydrogen evolution
Can Chang,Jicheng Wu,Dandan Wu,Guojian Jiang,Xiaowei Xu,Shufang Chang
DOI: https://doi.org/10.1039/d4nj00135d
IF: 3.3
2024-02-16
New Journal of Chemistry
Abstract:Graphitic carbon nitride (g-C 3 N 4 ), as a carbon support material with excellent stability and abundant active sites, has found widespread applications in various fields, including photocatalytic water splitting, electrolysis of water, and CO 2 reduction. Presently, research on the modification of g-C 3 N 4 primarily focuses on atomic doping, defect engineering, and the decoration of metal nanoparticles. In this study, a method involving the high-temperature pyrolysis of a solution containing thiourea and urea was successfully employed to synthesize sulfur-doped porous g-C 3 N 4 (S-C 3 N 4 ) nanosheets. Subsequently, PtCu nanoparticles were loaded onto the S-C 3 N 4 through a hydrothermal process. In the case of Pt loading of less than half of 20% Pt/C, this catalyst exhibited a low overpotential of only 10 mV at a current density of 10 mA cm −2 , which is significantly better than the 35 mV overpotential of 20% Pt/C. Furthermore, after a long period of continuous current stability testing, the overpotential of the catalyst did not increase by more than 30 mV, demonstrating excellent stability. The porous S-C 3 N 4 nanosheets possess a large specific surface area, providing abundant active sites for the HER reaction. This research introduces a fresh method for creating innovative catalysts based on Pt alloys supported by a carbon carrier.
chemistry, multidisciplinary