Abstract:A laser-assisted high-speed shearing (LAHSS) method has been proposed for metal bars, which prefabricates equally spaced fracture-start kerfs by Nd:Yag laser to make stress concentration, and applies a high-speed load to complete fracture separation. Comparative tests were conducted for Q235, 40Cr, and 304 steel bars, and the effects of fracture-start kerfs and axial clearance were investigated on the fracture section. Moreover, the fracture behavior was demonstrated by numerical simulation, and the micro-fracture mechanism was revealed by fractographic analysis. The numerical simulation results show that the material damage concentrates along with the kerf tips with peak equivalent plastic strain, and the corresponding stress triaxiality drops to almost zero at the kerf tip, which reveals that the material is subjected to pure shearing at kerf tip; the Max. loading force is reduced by 15.2%–29.6%, and the impact energy is decreased by 29.8%–46.9% for the three types of bar material. The experimental results showed that the fracture-start kerfs effectively inhibited the plastic deformation stage, and higher precision blanks were obtained in the LAHSS test: roundness error improved from 2.7%–10.9% to 1.1%–2.6%, Max. bending deflection decreased from 1.3–3.4 mm to 0.4–1.0 mm, and flatness error dropped from 0.9–3.3 mm to 0.3–0.7 mm. The fractographic analysis reveals that the crack initiation is related to alternative V-shape micro-notches at the laser-affected zone; the predominant fracture mechanism involves mode II microvoid coalescence at the main fracture plane; smaller and less elongated dimples were formed in 40Cr steels due to higher number density of grains and pinning effect of second-phase particles compared to Q235 and 304 steel bars.

Improvement of Experimental Device for Prefabricating V-shaped Notch Tip Crack

Feasibility investigation of ideal fracture caused by thermal stress

Numerical Study on Heat Stress Prefabricating Ideal Crack at the Bottom of V Shaped Notch in Precision Cropping

Numerical and Experimental Investigation of Notch-Induced High-Speed Precise Shearing of 42crmo Bar

Inner Damage Mechanism of Metal Bar with Thermal Stress

Investigation on the Crack Initiation of V-Shaped Notch Tip in Precision Cropping

A New Approach To Damage Modelling And Fracture Analysis For Metal Bar With V-Shaped Notch

The Causes and Control of Longitudinal Edge Cracks of the Plate

Experimental Study on New Low Cycle Fatigue Precision Cropping Process

Investigation of Notch-Induced Precise Splitting of Different Bar Materials under High-Speed Load

Experimental investigation on new low cycle fatigue precision cropping process

Research on the deflection of metal bar with V-shaped notch in low-stress cropping process

Influence of Cooling Water Temperature and Initial Heat Temperature of Bar on Heat Stress at the Bottom of V-Shaped Notch

Crack mechanism and experimental verification on straightening of AZ31B magnesium alloy plate

Fracture Strength of Metal Bars with Circumferential Notch

Prevention of transverse corner crack in continuous casting slab by adjusting cooling schedule

Rotary high-speed shearing cutting technology and experiment

Estimation of Crack Expansion Life of Bar V-shaped Norch Tip under Variable Amplitude Load

Investigation on Strain Fatigue Life of Metal Bar with V-shaped Notch in a Radial-forging Cropping Method

Investigation of Fracture Behavior and Mechanism in High-Speed Precise Shearing for Metal Bars with Prefabricated Fracture-Start Kerfs

Investigation on the influences of clearance and notch-sensitivity on a new type of metal-bar non-chip fine-cropping system