Abstract:Hierarchical meso-macroporous materials have attracted much attention due to their potential applications in catalysis, sorption, and separation. The incorporation of interconnected macropores in mesoporous materials is very useful because macropores can favor mass transfer and reduce transport limitations. However, it still remains a challenge to fabricate ordered mesoporous channels in the bicontinuous macroporous framework walls. This paper reports a double-templating route based on a sol-gel method to prepare hierarchical meso-macroporous silica monoliths. The obtained material shows a bicontinuous macroporous structure with highly ordered meso-channels distributing inside the macroporous skeleton walls. The bimodal pore structure was formed Under the action of the two templates. The organic polymer was added to induce a phase separation taking place at the sol-gel transition and thus form the bicontinuous macroporous structure. Meanwhile, a nonionic surfactant was introduced to template the formation of ordered mesostructure inside the macroporous skeleton walls. As characterization by scanning electron microscopy, transmittance electron microscopy, N-2,, physisorption, and X-ray diffraction, the resulting silica monolith exhibits Specific Surface area as high as 880 m(2)/g and pore volume as large as 1.2 cm(3)/g. The hexagonally ordered mesopores are highly centered at 5.8 nm. Besides, through optimizing the synthesis procedure, the monolith morphology of the resulting materials can be perfectly preserved during the wet gel drying process, and thus a crack-free hierarchical silica monolith with centimeter scale can be obtained.

Rational control of the micro/mesoporosity of multimodally porous carbon monoliths synthesized by nanocasting

Controlling the primary particle evolution process towards silica monoliths with tunable hierarchical structure.

Hierarchically macro/mesoporous silica monoliths constructed with interconnecting micrometer-sized unit rods

The Synthesis of Porous Materials with Macroscopically Oriented Mesopores Interconnected by Branched Mesopores

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Structurally Designed Synthesis of Mechanically Stable Poly(benzoxazine-co-resol)-Based Porous Carbon Monoliths and Their Application As High-Performance CO2 Capture Sorbents

Electron Microscopy and Nitrogen Adsorption Studies of Film-Type Carbon Replicas with Large Pore Volume Synthesized by Using Colloidal Silica and Sba-15 As Templates

Tunable Hierarchical Porous Silica Materials Using Hydrothermal Sedimentation-Aggregation Technique

Facile synthesis of highly graphitized porous carbon monoliths with a balance on crystallization and pore-structure

Spontaneous Preparation Of Hierarchically Porous Silica Monoliths With Uniform Spherical Mesopores Confined In A Well-Defined Macroporous Framework

Macro–mesoporous Silicas Complex and the Carbon Replica

Double-Templating Synthesis of Hierarchical Meso-Macroporous Silica Monolith

Precision Macroporous Monoliths Made Using High‐Throughput Microfluidic Emulsification

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Sponge-like carbon monoliths: Porosity control of 3D-printed carbon supports and its influence on the catalytic performance

Preparation of mesoporous carbon with adjustable diameter and pore size

3D Carbon Microspheres with a Maze-Like Structure and Large Mesopore Tunnels Built From Rapid Aerosol-Confined Coherent Salt/Surfactant Templating

Controllable Preparation of Monodisperse Mesoporous Silica from Microspheres to Microcapsules and Catalytic Loading of Au Nanoparticles

Self-Sacrificial Salt Templating: Simple Auxiliary Control over the Nanoporous Structure of Porous Carbon Monoliths Prepared through the Solvothermal Route

Functional silica monoliths with hierarchical uniform porosity as continuous flow catalytic reactors

Controlled Synthesis of N-Doped Carbon Nanospheres with Tailored Mesopores through Self-Assembly of Colloidal Silica.