Abstract:Morphology and crystalline-phase control of titanium dioxide is a crucial issue in the study of photocatalytic activity. Here, we present a facile synthetic path combing the solgel method with solvothermal treatment to form hybrid mesoporous and microporous TiO2. The TiO2 precursor was obtained by the solgel method, and this was self-assembled into mesopores and micropores by NH4F corrosiveness on the surface of TiO2 under hydrothermal conditions. Powder X-ray diffraction (XRD), thermogravimetric analysis and differential scanning calorimetry (TGA/DSC), X-ray photoelectron spectroscopy (XPS), N-2 adsorption measurements, transmission electron microscopy (TEM) and Raman spectroscopy were used to characterise the titania powders. The results reveal that NH4F not only improved the formation of the crystallised anatase phase but also served as a corrosive agent modified on the surface of TiO2 precursors. Defective voids among these nanoparticles formed micropores by hydrothermal reaction of NH4F and TiO2 over a long time. When the NH4F concentration was 1.0 mol.L-1, micropores became dominant,and few mesopores were obtained, and this results in a smaller average pore size. Thus, mesoporous and microporous structures were formed. Furthermore, these crystallised mesoporous and microporous anatase titania nanoparticles with uniform structure and high surface area have a higher photocatalytic activity for azo dye degradation under near UV irradiation.

Study on the Preparation of Ultrafine Mesoporous TiO2 with Controllable Crystalline Phase and Its Photocatalytic Activities

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Synthesis, Characterization and Photocatalysis of Mesoporous Tio2

Preparation and Performance of Mesoporous TiO<sub>2</sub> Photocatalyst with P123 As Template

Preparation and photocatalytic activity of mesoporous TiO2 derived from hydrolysis condensation with TX-100 as template

Characterization of Mesoporous Nanocrystalline TiO2 Photocatalysts Synthesized Via a Sol-Solvothermal Process at a Low Temperature

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Synthesis of Well-Ordered Mesoporous Titania with Tunable Phase Content and High Photoactivity

Sonochemical Synthesis and Photocatalytic Activity of Meso- and Macro-Porous TiO(2) for Oxidation of Toluene.

Preparation of NanoTiO2 Photocatalyst Sol

Preparation and Characterization of Highly Active Mesoporous TiO2 Photocatalysts by Hydrothermal Synthesis under Weak Acid Conditions

Preparation of TiO2/mesoporous Carbon Composites and Their Photocatalytic Performance for Methyl Orange Degradation

Acid-regulated hydrolysis and condensation of titanium cation toward controllable synthesis of multiphase mesoporous TiO2 for effectively enhance photocatalytic H2 evolution

Sol-Gel Preparation and Characterization of High Activity Titanium Dioxide Nanocrystalline Photocatalyst

Synthesis and characterization of visible light driven mesoporous nano-photocatalyst MoO 3/TiO 2

Ultrasonic preparation of mesoporous titanium dioxide nanocrystalline photocatalysts and evaluation of photocatalytic activity

UV/ozone-assisted Low Temperature Preparation of Mesoporous TiO2with Tunable Phase Composition and Enhanced Solar Light Photocatalytic Activity

Preparation of Mesoporous Titanium Dioxide Using a Composite Surfactant Template and Super-Critical Desiccation Technique

Mesoporous Spherical TiO2 with Outstanding Photocatalysis under Visible Light

Synthesis of Titanium Dioxide and the Study of Photocatalytic Activity

Preparation of TiO2 Nanofilm Via Sol–gel Process and Its Photocatalytic Activity for Degradation of Methyl Orange