Abstract:Monodispersed crosslinked cationic poly(4-vinylpyridine-co-butyl acrylate) [P(4VP-BA)] seed latexes were prepared by soapless emulsion polymerization, using 2,2'-azobismethyl(propionamidine)dihydrochloride (V-50) as an initiator and divinylbenzene (DVB) or ethylene glycol dimethacrylate (EGDMA) as a crosslinker. The optimum condition to obtain monodispersed stable latex was investigated. It was found that the colloidal stability of the P4VP latex can be improved by adding an adequate amount of BA (BA/4VP = 1/4, w/w), and adopting a semicontinuous monomer feed mode. Subsequently, poly(4-vinylpyridine-co-butyl acrylate)/Poly(styrene-co-butyl acrylate) [P(4VP-BA)/P(ST-BA)] composite microspheres were synthesized by seeded polymerization, using the above latex as a seed and a mixture of ST and BA as the second-stage monomers. The effects of the type of crosslinker, the degree of crosslinking, and the initiators (AIBN and V-50) on the morphology of final composite particles are discussed in detail. It was found that P(4VP-BA)/P(ST-BA) composite microspheres were always surrounded by a PST-rich shell when V-50 was used as initiator, while sandwich-like or popcorn-like composite particles were produced when AIBN was employed. This is because the polarity of the polymer chains with AIBN fragments is lower than for the polymer with V-50 fragments, hence leading to higher interfacial tension between the second-stage PST-rich polymer and the aqueous phase, and between PST-rich polymer and P4VP-rich seed polymer. As a result, the seed cannot be engulfed by the PST-rich polymer. Furthermore, the decrease of T-g of the second-stage polymer promoted phase separation between the seeds and the PST-rich polymer: sandwich-like particles formed more preferably than popcorn-like particles. It is important knowledge that various morphologies different from PST-rich core/P4VP-rich shell morphology, can be obtained only by changing the initiator, considering P4VP is much more hydrophilic than PST. The zeta potential of composite particles initiated by AIBN in seeded polymerization shifted from a positive to a negative charge. (C) 2002 John Wiley & Sons, Inc. J Appl Polym Sci 83: 1190-1203, 2002.

In Situ Preparation and Properties of High‐solid‐content and Low‐viscosity Poly(methyl Methacrylate/n‐butyl Acrylate/acrylic Acid)/poly(styrene/acrylic Acid) Composite Latexes

Seed Semicontinuous Emulsion Multi-Copolymerization of (meth)acrylates with High-Solid Content - Effect of the Operation Conditions

Preparation and Characterization of MMA-BA-DMAEMA Terpolymer Latex

Preparation of CO2/N2‐Triggered Reversibly Coagulatable and Redispersible Polyacrylate Latexes by Emulsion Polymerization Using a Polymeric Surfactant

Macromol. Rapid Commun. 10/2012

Switchable Block Copolymer Surfactants for Preparation of Reversibly Coagulatable and Redispersible Poly(Methyl Methacrylate) Latexes

Preparation of Mma-Ba-Dmaema Nanosized Latex

Synthesis and Characterization of Poly(butyl Acrylate)/silica and Poly(butyl Acrylate)/silica/poly(methyl Methacrylate) Composite Particles

Morphologies and Dynamic Mechanical Properties of Core‐shell Emulsifier‐free Latexes and Their Copolymers for P(BA/MMA)/P(MMA/BA) and P(BA/MMA)/PSt Systems in the Presence of AHPS

Convenient Synthesis and Morphology of Latex Particles Composed of Poly (methyl Methacrylate)-B-Poly (N-Butyl Acrylate) by 1, 1-Diphenylethylene (dpe) Seeded Emulsion Polymerization

Characterization and Particle Size Control of Acrylic Polymer Latex Prepared with Green Surfactants

Preparation and Characterisation of Novel Cross-Linked Poly (IBOMA-BA-DFMA) Latex

Emulsion copolymerization of MMA/BA in the presence of surface active monomers (III) - Latex stability

Preparation Of A Silica/Poly(N-Butyl Acrylate-Co-Acrylic Acid) Composite Latex And Its Pressure-Sensitive Properties

Morphology and Formation Mechanism of Poly(butyl Acrylate)/nanosilica Composite Particles Prepared by in Situ Emulsion Polymerization

Preparation and Properties of Silicone-Acrylate Copolymer Latex

Preparation of Composite Latexes with Different Core Components and the Influence on the Pressure-Sensitive Properties

PREPARATION AND PROPERTY STUDY OF HIGH-SOLID-CONTENT AND LOW-VISCOSITY P(MMA/BA/AA) EMULSIONS

Synthesis and Characterization of Polyacrylate Modified by Polysiloxane Latexes and Films

Studies on the Preparation of Stable and High Solid Content Emulsifier‐free Latexes and Characterization of the Obtained Copolymers for MMA/BA System with the Addition of AHPS

Study on Synthesis and Morphology Control of Poly(4‐vinylpyridine‐co‐butyl Acrylate)/poly(styrene‐co‐butyl Acrylate) Composite Microspheres