Dual properties of microwave absorption and thermal protection in La0.5Sr0.5FeO3‐Al2O3 pseudo‐binary composites
Peng Wu,Wenting He,Yuyi Gao,Jie Xiao,Liangliang Wei,Hongbo Guo
DOI: https://doi.org/10.1002/adem.202300264
IF: 3.6
2023-05-06
Advanced Engineering Materials
Abstract:As multifunctional material for microwave absorption and thermal protection, the dielectric and thermophysical properties of equilibrium phases in LSF(La0.5Sr0.5FeO3)‐Al2O3 pseudo‐binary phase diagram were investigated in the present work. Four pseudo‐binary composites were obtained by sintering at 1400 °C for 10 h with different raw components (x wt% LSF‐(100‐x) wt% Al2O3, x=20, 40, 60 and 80), labeled as LSFA20, LSFA40, LSFA60 and LSFA80, respectively. After sintering, the main equilibrium phase in LSFA20 and LSFA40 composites was SrAl12O19‐based solid solution. For LSFA60 and LSFA80, however, LSF‐based and SrAl12O19‐based solid solutions are the main equilibrium phases. The increase of conductive LSF content resulted in the highest dielectric loss tangent and the best microwave absorbing property in LSFA80, in which the bandwidths for reflection loss less than ‐10 dB and ‐5 dB are about 2.37 GHz and 7.7 GHz, respectively, when the thickness is only 1.5 mm. The thermophysical properties reveals that the thermal conductivity in LSF‐Al2O3 pseudo‐binary composites shows weak temperature dependence because of the opposite contribution between phonon and electron. It is lower than that of traditional thermal barrier coating material of 8 wt% Y2O3‐stabilized zirconia (8YSZ). This article is protected by copyright. All rights reserved.
materials science, multidisciplinary