The Preparation and Characterization of Zn-Ca System Phosphating Film Without Washing at the Room Temperature

YU Qu-min,LI Rong-xi,WANG Li-ping

DOI: https://doi.org/10.3969/j.issn.1000-2537.2007.01.014

2007-01-01

Abstract:The Zn-Ca system phosphating solution is composed of H3PO4,ZnO,Ca(NO3)2·4H2O,Ba(NO3)2,(NH4)6Mo7O24·4H2O and so on,which react with each other to produce phosphating film,sediment and volatile.The Zn-Ca system phosphating solution is fast occurred phosphating reaction on steel acted as matrix and then was dried for more than 2 h to produce colour Zn-Ca System phosphating film.The phosphating film was characterized by means of SEM,XPS,rust,and smear.The results show that the phosphating film without washing is composed of phosphate with Fe3+,Zn2+ and Ca2+.The phosphating film,whose crystalline size is small than or equal to 2 μm,is series and thick with weightiness of 1.2 g·m-2.It bears corrupt of NaCl solution with 3% for about 2.5 h.The cling force of phosphating film,smeared by lacquer of epoxy resin antirust of iron oxide red,reaches stair,and the quality of the phosphating film is more than that of phosphating film prepared by traditional technology,i.e.washing after phosphating reaction.