Abstract:In order to study the durability of concrete materials subjected to sulfate attack, in a sulfate attack environment, a series of concrete tests considering different fly ash contents and erosion times were conducted. The mechanical properties and the micro-structure of concrete under sulfate attack were studied based on the following: uniaxial compressive strength test, split tensile test, ultrasonic impulse method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The mechanical properties were compressive strength, splitting tensile strength, and relative dynamic elastic modulus, respectively. Additionally, according to the damage mechanical theory, experimental results and micro-structure analysis, the damage evolution process of concrete under a sulfate attack environment were studied in detail. Finally, according to the sulfate attack time and fly ash content, a damage model of the sulfate attack of the binary surface was established. The specific results are as follows: under the action of sulfate attack, the change law of the rate of mass change, relative dynamic modulus of elasticity, corrosion resistance coefficient of compressive strength, and the corrosion resistance coefficient of the splitting tensile strength of concrete all increase first and then decrease. Under the same erosion time, concrete mixed with 10% fly ash content has the best sulfate resistance. Through data regression, the damage evolution equation of the sulfate attack was developed and there is an exponential function relationship among the different damage variables. The binary curved surface regression effect of the concrete damage and the erosion time and the amount of fly ash is significant, which can predict deterioration of concrete damage under sulfate attack. During the erosion time, the combined expansion of ettringite and gypsum caused micro cracks. With an increase of corrosion time, micro cracks developed and their numbers increased.

The changes of the nonclassical nonlinear effect under erosion of sulfate

Study on the Deterioration of Concrete under Dry-Wet Cycle and Sulfate Attack

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Mechanical Properties and Damage Evolution of Concrete Materials Considering Sulfate Attack

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Research on the performance evolution of concrete under the coupling effects of sulfate attack and carbonation

Concrete damage diagnosed using the non-classical nonlinear acoustic method

Modeling nonlinear stress-strain model for sulfate dry-wet cycle erosion of concrete: considerations for the initial compaction stage

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

The Study on the Nonclassical Nonlinear Effect of Concretes with Different Mix Rate

Damage Evolution of Concrete under the Actions of Stray Current and Sulphate

Effects of Sodium Sulfate Attack on Concrete Incorporated with Drying-Wetting Cycles

Damage evolution behavior of tunnel lining concrete with non‐through crack under single‐sided sulfate attack

Combined effects of sulfate attack under drying–wetting cycles and loading on the fatigue behavior of concrete

Concrete Deterioration Mechanisms under Combined Sulfate Attack and Flexural Loading

The Influence of Sulfate Attack on the Dynamic Properties of Concrete Column

Study on the deterioration of concrete performance in saline soil area under the combined effect of high low temperatures, chloride and sulfate salts

Decay of fracture parameters of concrete under sulfate environments

Experimental study on underground structure concrete under static bending loads and sulfate attack

Nondestructive Assessment of Microcracks Detection in Cementitious Materials Based on Nonlinear Ultrasonic Modulation Technique