Abstract:Gallium nitride (GaN) nanostructures were successfully synthesized by the nitridation of the electrochemically deposited gallium oxide (Ga2O3) through the utilization of a so-called ammoniating process. Ga2O3 nanostructures were firstly deposited on Si substrate by a simple two-terminal electrochemical technique at a constant current density of 0.15 A/cm(2) using a mixture of Ga2O3, HCl, NH4OH and H2O for 2 h. Then, the deposited Ga2O3 sample was ammoniated in a horizontal quartz tube single zone furnace at various ammoniating times and temperatures. The complete nitridation of Ga2O3 nanostructures at temperatures of 850°C and below was not observed even the ammoniating time was kept up to 45 min. After the ammoniating process at temperature of 900°C for 15 min, several prominent diffraction peaks correspond to hexagonal GaN (h-GaN) planes were detected, while no diffraction peak of Ga2O3 structure was detected, suggesting a complete transformation of Ga2O3 to GaN. Thus, temperature seems to be a key parameter in a nitridation process where the deoxidization rate of Ga2O3 to generate gaseous Ga2O increase with temperature. The growth mechanism for the transformation of Ga2O3 to GaN was proposed and discussed. It was found that a complete transformation can not be realized without a complete deoxidization of Ga2O3. A significant change of morphological structures takes place after a complete transformation of Ga2O3 to GaN where the original nanorod structures of Ga2O3 diminish, and a new nanowire-like GaN structures appear. These results show that the presented method seems to be promising in producing high-quality h-GaN nanostructures on Si.

Catalytic synthesis of single-crystalline gallium nitride nanobelts

Synthesis and characterization of crystalline gallium nitride nanoribbon rings

A Study On Self-Assembled Gan Nanobelts By A New Method: Structure, Morphology, Composition, And Luminescence

A simple method for the growth of high-quality GaN nanobelts

Two-step synthesis of one-dimensional single crystalline GaN nanowires

Large-scale Synthesis of Single-Phase, High-Quality GaN Nanocrystallites

Large-scale Synthesis of GaN Nanorods and Their Photoluminescence

Catalytic Growth of Gallium Nitride Nanowires on Wet Chemically Etched Substrates by Chemical Vapor Deposition

A simple method to synthesize gallium oxide nanosheets and nanobelts

From powder to nanowire: A simple and environmentally friendly strategy for optical and electrical GaN nanowire films

Rapid synthesis of gallium nitride powder

Defect-pit-assisted Growth of GaN Nanostructures: Nanowires, Nanorods and Nanobelts

Synthesis Of Gallium Nitride Nanorods Through A Carbon Nanotube-Confined Reaction

Simple And High-Yield Method For Synthesizing Single-Crystal Gan Nanowires

Synthesis of gallium nitride nanostructures by nitridation of electrochemically deposited gallium oxide on silicon substrate

Pyrolysis Approach to the Synthesis of Gallium Nitride Nanorods

Synthesis of single crystalline GaN nanoribbons on sapphire (0001) substrates

High-Quality Gan Nanowires Synthesized Using A Cvd Approach

Controllable Synthesis of SnO2 Nanowires and Nanobelts by Ga Catalysts

Rapid Synthesis of High Purity Gan Powder

Preparation of Gan Nanowires by Nonammonia Method and Their Photoelectronic Properties