PREPARATION OF ANTIBACTERIAL POLYSULFONE ULTRAFILTRATION MEMBRANE BY GRAFTING CAPSAICIN DERIVATIVE VIA SURFACE UV IRRADIATION

Meng Zhuang,Gao Xueli,Wang Jian

DOI: https://doi.org/10.3969/j.issn.1000-3770.2013.09.009

2013-01-01

Abstract:The N-(2,3,4-top oxygen base benzyl)acrylamide(TMBA) and acrylic acid(AA) were grafted onto polysulfone(PSF) ultrafiltration(UF) membrane using benzophenone(BP) as the initiator to improve the antibacterial and antifouling property.For modifications of PSf UF membranes,only UV light with λ> 300 nm,or better λ> 350 nm,can be recommended,because the polymer chain scission was suppressed by H-abstraction from methyl groups under long-wavelength UV irradiation(λ>300 nm),which avoided the photodegradation of PSF ultrafiltration membrane.Based on the previous experience,the effects of BP concentration to the modified PSF UF membrane were investigated by keeping the UV irradiation time as 15 min,TMBA and AA concentration as 1% and 2% respectively.The changes on the structure and properties were studied by measuring flux and rejection,contact angle(CA),Fourier transform infrared spectroscopy(FTIR-ATR),Scanning Electron microscope(SEM),and antibacterial analysis.The success grafting TMBA and AA onto the surface of PSF UF membranes was verified by the presence of infrared absorption band at 1 645 cm-1and 1 720 cm-1.The egg albumin rejection rate of the PSF UF membrane was increased from 89% to 96%,while pure water flue was still fine,with the increasing of BP concentration from 0 to 0.2%.At the same time,the recovery rate of pure water flux of the egg album fouled membranes increased from 25% to 80% after water flushing,which represented an enhancing of membrane antifouling property.The number and size of membrane pore decreased obviously,which explained the increase of rejection and the decrease of pure water flue.Escherichia coli was chosen to test the antibacterial activity of the membranes.Due to the antibacterial activity of TMBA,the modified membranes showed an enhancing antibacterial efficiency.The antibacterial efficiency was up to 95% when the BP concentration was 0.2%,while that of the unmodified membrane was only 21%.It was proved by the results that the PSF ultrafiltration membrane gained better properties after modifying by UV irradiation.