Abstract:Single-crystalline perovskite BaTiO3 (BTO) nanorods were synthesized by (BaTi2O5-template) molten salt synthesis (MSS) methods. The effects of process parameters (eg, calcination temperature, reaction time, molten salt content, as well as different phase structures of TiO2 and barium oxides) on the formation of BTO nanorods and their structural characteristics were systematically investigated. The BTO nanorods synthesized at 800 degrees C for 5 hours by MSS method with the molar salt ratios of BaCO3:TiO2 (anatase):NaCl:KCl equal to 1:1:60:60, exhibited smooth and clean surfaces through their lengths. Their diameters were in the range of 130-200 nm with average length of 5 mu m. Large-scale amount of BTO nanorods was synthesized by BaTi2O5-template MSS method at 650 degrees C with molar salt ratios of BaC2O4:BaTi2O5 (template):NaCl:KCl equal to 1:1:60:60. The BTO nanorods successfully retained the one-dimensional morphology of the BaTi2O5 templates and their lengths were in the range of 5-10 mu m with an average diameter of similar to 300 nm. The single-crystalline nature of individual BTO nanorod was revealed by its selected area electron diffraction patterns and high-resolution TEM images. The BTO nanorods exhibited good optical properties with optical bandgaps in the range of 2.5-2.6 eV. Such optical bandgaps make the present BTO nanorods promising candidates for ferroelectric photovoltaic devices. Dielectric properties of the BTO nanorods synthesized by MSS method were comparatively investigated with the BTO nanorods synthesized by the BaTi2O5-template MSS method. It is found that the later BTO nanorods exhibit better dielectric properties and their synthesized temperature is also much lower than the former ones.

General surfactant-free synthesis of MTiO3 (M = Ba, Sr, Pb) perovskite nanostrips

General approach to well-defined perovskite MTiO3 (M = Ba, Sr, Ca, and Mg) nanostructures

Surfactant-Free Synthesis of Single-Crystalline Bi4Ti3O12 Nanosheets with Excellent Visible-Light Photocatalytic Activity

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

A Surfactant-Free Route to Synthesize Ba X Sr 1− X TiO 3 Nanoparticles at Room Temperature, Their Dielectric and Microwave Absorption Properties

Hydrothermal Synthesis of Single-Crystalline Perovskite PbTiO3 Nanosheets with Dominant (001) Facets

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Shape-Controlled Synthesis of Mnwo4 Nanocrystals by A Surfactant-Free Hydrothermal Method

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Synthesis of Single-Crystal Ba1−xSrxTiO3 (x = 0–1) Dendrites Via a Simple Hydrothermal Method

Solvent-controlled Synthesis of Three-Dimensional TiO2 Nanostructures Via a One-Step Solvothermal Route

Synthesis of Perovskite Structure (Ca-0.61, Nd-0.26)TiO3 Nanopaticles by Sol-Gel Method

Molten Salt Synthesis of BaTiO3 Nanorods: Dielectric, Optical Properties, and Structural Characterizations

One-Atmosphere Aqueous-Solution Synthesis of Trimolybdate Nanomaterials and the Feasibility for Mass Production

Synthesis and characterization of ordered hexagonal and cubic mesoporous tin oxides via mixed-surfactant templates route.

Surfactant‐Free Synthesis of Crystalline Mesoporous Metal Oxides by a Seeds/ NaCl‐Mediated Growth Strategy

Stabilization of Sr 3 Al 2 O 6 Growth Templates for Ex Situ Synthesis of Freestanding Crystalline Oxide Membranes

Surfactant-Free Synthesis of Three-Dimensional Perovskite Titania-Based Micron-Scale Motifs Used as Catalytic Supports for the Methanol Oxidation Reaction

Synthesis of Single-Crystalline Barium Dititanate Nanobelts

Surface properties of atomically flat poly-crystalline SrTiO3

Synthesis of mesoporous strontium titanate by molten salt assisted template-free method