Preparation and Kinetics of Non-Isothermal Crystallization of Co77.5Si13.5B9 Amorphous Alloys

郝雷,刁训刚,王天民

DOI: https://doi.org/10.3969/j.issn.0258-7076.2008.04.011

2008-01-01

Abstract:The investigation on Co-based amorphous alloys was a foreland of condensation physics and for design of new materials with uniformly physical and chemical properties.In this paper,the Co-based amorphous alloys were prepared by rapid cooling on a single Cooper wheel in air atmosphere.The results of XRD and TEM analyses indicated that the alloy specimen was fully amorphous.The thermal stability and crystallization behavior of the alloy was studied by using the differential thermal analysis(DTA) in argon atmosphere,and glass transition temperature(Tg),crystallization temperatures(Txi),peak temperatures(Tpi) were determined at the heating rate of 5,10,15,35,55,75 and 95 K·min-1,respectively.It was found that Tg,Txi,Tpi of the amorphous alloy depended on the heating rate during the continuous heating,which suggested that both glass transition and crystallization had a significant kinetic effect.The kinetics of non-isothermal crystallization at constant heating rate,such as apparent crystallization activation energy,could be analyzed by the Kissinger and Doyle-Ozawa methods.A detailed interpretation of the results led to some interesting conclusions.The important results obtained were as follows: From the non-isothermal DTA thermo gram,it could show that the value of peak temperature of crystallization of the alloy increased with heating rate increasing.The apparent activation energy was variation with Tg,Tx and Tp suggested by Kissinger method.The average activation energy suggested by Doyle-Ozawa was similar as that obtained by Kissinger method.The curves of relation of crystallized fraction x with temperature or time at different heating rates exhibited as a function of "S" shape.