Abstract:The cathode materials of spinel LiMn2O4 coated with 1.5(wt)%Al2O3 and Al doped LiAlxMn2-xO4(x=0.1,0.2,0.3,0.4)were synthesized.The structures and morphologies of the as-prepared materials were characterized by X-ray diffraction(XRD) and Field scanning electron microscopy(FSEM).The results showed that the diffraction of LiMn2O4 modified is similar,with all the peaks index able in the Fd3m space group,but the positions of the diffraction peak shift to higher angle;Al2O3particles appear on the surface of the coated spinel LiMn2O4and powders of Al doped LiMn2O4have the uniform,nearly cubic structure morphology with narrow size distribution which is less than 500nm.Galvanostatic charge-discharge test indicated that cycle performance of LiMn2O4 can be improved significantly after coated or doped.Among all modified samples,LiMn2O4 coated with 1.5(wt)%Al2O3 and LiAl0.2Mn1.8O4had the better electrochemical performance and same initial discharge capacity of 99.7 mAh/g.The capacities retained of 87.4% and 88.4% after 50 cycles,respectively.In initial charge,the EIS of LiAl0.3Mn1.7O4 electrode consist of the semicircle of high frequency region and a arc of low frequency region which continue to narrow as increasing of polarization potential,to evolve into the semicircle at 3.95V and at same time the slash related with the lithium-ion diffusion in the EIS low frequency region emerge.The resistance of SEI film and the thickness of SEI were decrease with the increase of polarization potential,but the charge transfer resistance Rct was first decreasing and then increasing and LiAl0.4Mn1.6O4 had smaller Rct than that of LiAl0.3Mn1.7O4corresponding to the extraction of Li+ions.

Synthesis and Electrochemical Performances of Spinel LiMn_(2-x)In_xO_4(x=0,0.01,0.02,0.05)

Synthesis and Electrochemical Characterizations of Spinel LiMn2O4 by Citric Acid-Assisted Sol-Gel Method

Synthesis of spinel LiMn2-xGaxO4 and their electrochemical characterisitics

Structure and electrochemical properties of LiMgxMn2-xO4 cathode materials for Li-ion batteries

Electrochemical Performance Ni Doped Spinel LiMn2O4 Cathode for Lithium Ion Batteries

Synthesis of Spinel Linixmn2-Xo4 (X=0, 0.1, 0.16) and Their High Rate Charge-Discharge Performances

Synthesis and Physicochemical Properties of LiLa0.01Mn1.99O3.99F0.01 Cathode Materials for Lithium Ion Batteries

Synthesis And Electrochemical Performance Of Linixmn2-Xo4 Spinel As Cathode Material For Lithium Ion Batteries

Electrochemical Performance of Spinel LiMn_2O_4 Modified

Structural and electrochemical characterization of LiMn2-2xLixNixO4 (0 <= x <= 0.1) cathode materials

Physical Properties and Electrochemical Performance of Linixmn2-Xo4 Cathode Materials Prepared

Changes in Mn3+/Mn4+ Ratio, Resistance Values in Electrochemical Impedance Spectra, and Rate Capability with Increased Lithium Content in Spinel LixMn2O4

Synthesis and electrochemical characterizations of spinel LiMn 1.94 MO 4 (M = Mn 0.06 , Mg 0.06 , Si 0.06 , (Mg 0.03 Si 0.03 )) compounds as cathode materials for lithium-ion batteries

Structure and Electrochemical Performance of Modificated LiMn<sub>2</sub>O<sub>4</sub> by S-Co Codoping and Nano SiO<sub>2</sub> Surface Coating

Effects of equimolar Mg (II) and Si (IV) co-doping on the electrochemical properties of spinel LiMn2−2xMgxSixO4 prepared by citric acid assisted sol–gel method

Synthesis and electrochemical characterization of multi-cations doped spinel LiMn2O4 used for lithium ion batteries

Effect of Lithium Content on the Electrochemical Properties of Solid-State-synthesized Spinel LixMn2O4

Physical Properties and Electrochemical Performance of LiNi X Mn 2-X O 4 Cathode Materials Prepared Using a Precipitation Method

Preparation and Electrochemical Properties of X Li2MnO3·(1-x)LiMn2O4 Composites

Structure and Electrochemical Performance of Modificated LiMn2O4 by S-Co Codoping and Nano SiO2 Surface Coating

Electrochemical Performance of LiMn_(2-x)Co_xO_4 Cathode Materials Synthesized by a Co-Precipitation Method