Abstract:In this work, the hydrogen desorption properties of the novel Mg-Al-H hydrogen storage composites prepared by ball-milling the as-received magnesium hydride (MgH2) and the as-prepared aluminum hydride (AlH3) with different molar ratios (1:1, 1:0.5, and 1:0.25) are investigated systematically. Nonisothermal desorption measurements show that more than 7.51 wt % of hydrogen is released from the Mg-Al-H composites when they are heated from room temperature to 500 degrees C. Thermal analysis by differential scanning calorimeter (DSC) and hydrogen desorption spectrum by mass spectrometer (MS-H-2) are used synchronously to study the desorption process of the Mg-Al-H. The onset hydrogen desorption temperature of MgH2 in the MgH2 + AlH3 composite is dramatically reduced from 320 degrees C for the pure MgH2 to below 252 degrees C. The DSC/MS-H-2 and the X-ray diffraction (XRD) analyses show that the desorption of MgH2 in the Mg-Al-H composite is composed of two steps with the reaction between MgH2 and Al forming Mg17Al12 as the first step and the self-decomposition of the residual MgH2 as the second step. Isothermal desorptions show that the desorption kinetics of the MgH2 in the Mg-Al-H composite is significantly improved. The apparent activation energy for the desorption of MgH2 in the MgH2 + 0.25AlH(3) is reduced to 144.6 kJ/mol, which contributes to the improvement in the desorption kinetics of MgH2. The Johnson-Mehl-Avrami (JMA) kinetic studies indicate that the desorption kinetic model of MgH2 in the Mg-Al-H composite is different from the pure MgH2. Concerning the reversibility, under the conditions of 300 degrees C and 5 MPa H-2, MgH2 in the Mg-Al-H composite is almost fully recovered after absorption for 5 h while it is partially recovered for the pure MgH2. Among the samples studied, the MgH2 + 0.25AlH(3) composite exhibits the highest reversible hydrogen storage capacity of 6.10 wt % (H/M).

Mg3Mm Compound Based Hydrogen Storage Materials

Hydrogen desorption properties of the MgH2-AlH3 composites

The hydrogen storage behavior of Mg3La and Mg3LaNi0.1

Effect of Ni on Mg Based Hydrogen Storage Alloy Mg3Nd

Hydrogen Storage Behaviors and Microstructure of MF3 (m=ti, Fe)-doped Magnesium Hydride

Hydrogen Storage Properties of Mg-doped Ti 1.2 Fe Alloys Synthesized by Mechanical Alloying

Hydrogen Storage Behavior of Mg3La and the Effect of Ni Addition on It

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Structure and Hydrogen Storage Properties of Mg3Pr and Mg3PrNi0.1 Alloys

An Investigation on the Reaction Mechanism of LiAlH4–MgH2 Hydrogen Storage System

Numerical Simulation of Intrinsic Absorption and Desorption Kinetics for Mg-3Ni-2MnO_2 Hydrogen Storage Materials

Effect Of Mg On The Hydrogen Storage Characteristics Of M1(1-X)Mg(X)Ni(2.4)Co(0.6) (X=0-0.6) Alloys

A New Type of Mg-based Metal Hydride with Promising Hydrogen Storage Properties

Hydrogen sorption properties of Mg/Mm–Ni multi-layer film prepared by thermal evaporation

Comparative Investigation on the Hydrogenation/Dehydrogenation Characteristics and Hydrogen Storage Properties of Mg3ag and Mg3y

Hydrogen-Induced Reversible Phase Transformations and Hydrogen Storage Properties of Mg–Ag–Al Ternary Alloys

Reversible De/hydriding Reactions Between Two New Mg–In–Ni Compounds with Improved Thermodynamics and Kinetics

Hydrogen Storage Properties of Mg and Mg-Ni Films Prepared by Thermal Evaporation

Ternary Mg-Nb-H polyhydrides under high pressure

Hydrogen storage properties of Mg-23.3wt.%Ni eutectic alloy prepared via hydriding combustion synthesis followed by mechanical milling

Hydrogen Storage Properties of Mg100−xNix (x = 5, 11.3, 20, 25) Composites Prepared by Hydriding Combustion Synthesis Followed by Mechanical Milling (HCS + MM)