Luminescence properties of Eu2+ doped β-SiAlON phosphor
Li Li,Cheng Zhang,Danyu Jiang,Na Zhang,Caixia Li,Qiang Li
DOI: https://doi.org/10.4028/www.scientific.net/KEM.492.320
2012-01-01
Key Engineering Materials
Abstract:Eu2+ doped β-SiAlON (z = 1, 3, 4) phosphor were synthesized by carbothermal reduction-nitridation (CRN) using precursors powder as materials. The precursors powder prepared by sol-gel method using the SiO 2, AlCl3·6H2O, Eu(NO3) 3, ammonia water, carbon powders as starting materials. The CRN reaction proceeded at 1380°C for 6 h in an N2 atmosphere. Eu 2+ doped β-SiAlON (z = 1, 3, 4) had high adsorption in the UV-visible spectral region. While z = 1, one bands were observed in the emission spectrum centered at about 425 nm monitored at 282 nm. The excitation bands centered at about 282 nm. While z = 3, one bands were observed in the emission spectrum centered at about 425 nm monitored at 282 nm. The excitation bands centered at about 282 nm. While z = 3, the emission spectra exhibit one bands with maxima at about 419 nm under 280 nm excitation. The excitation bands centered at about 280 nm. While z = 4, the emission spectrum centered at about 419 nm monitored at 280 nm. The excitation bands centered at about 280 nm. In this work, luminescence properties of Eu2+ doped β-SiAlON (z = 1, 3, 4) are independent of z value. It is possible related to the low synthesis temperature. © (2012) Trans Tech Publications.