Preparation and modification of water-dispersible epoxy curing agent

LIU Gang,HUI Hai-jun,ZHOU Zi-hu,SUN Zai-wu,LIU Ya-li
DOI: https://doi.org/10.19289/j.1004-227x.2009.10.015
2009-01-01
Abstract:A reactive emulsifier was synthesized through the reaction of liquid epoxy resin EPON828 and polyethylene glycol(PEG) with different molecular weight,and then used as a chain extender to react with the amine-terminated intermediate prepared with EPON828 and m–xylylenediamine(MXDA) . After the amine-terminated curing agent was end-capped with reactive diluent,a water-dispersible epoxy curing agent was obtained by adding water continuously. The water-dispersible epoxy curing agent was modified by silane coupling agent KH-550(namely 3–aminopropyltriethoxysilane) . The molar ratio of MXDA to EPON828 was determined as 2.2:1. The dispersion of waterborne epoxy curing agent,which was prepared using 9% reactive emulsifier synthesized withPEG6000 and EPON828 at an equivalent molar ratio and modified with silane coupling agent KH-550 with an amount of 2% of the dispersion,had optimal stability and following properties:particle size ca.750.8 nm,solid content 60%,amine value 118 mgKOH/g,and viscosity 4 500 mP·s. The coating cured at room temperature had a hardness 3H,60° gloss 108%,impact strength 50 kg·cm,flexibility 1 mm,adhesion strength 1 grade,and good resistance to acid and alkali corrosion. The product was characterized by Fourier transform infrared spectroscopy.
What problem does this paper attempt to address?