Ordered Mesoporous Titanosilicates with Better Catalytically Active Titanium Sites Assembled from Preformed Titanosilicate Precursors with Zeolite Building Units in Alkaline Media
KF Lin,ZH Sun,L Sen,DZ Jiang,FS Xiao
DOI: https://doi.org/10.1016/j.micromeso.2004.04.025
IF: 5.876
2004-01-01
Microporous and Mesoporous Materials
Abstract:Mesostructured titanosilicates have been successfully synthesized from the assembly of preformed titanosilicate precursors with CTAB surfactant micelle in both alkaline media (MTS-5) and strongly acidic media (MTS-8). The samples were characterized by powder X-ray diffraction (XRD), nitrogen isotherms, 29Si MAS NMR, IR, and UV–visible spectroscopy. These materials exhibit highly hydrothermal stability, as compared with Ti-MCM-41. Characterization results indicate that these mesostructured titanosilicates of MTS-5 and MTS-8 have TS-1-like titanium species, and that the mesoporous walls contain the primary and secondary building units similar to those in microporous crystal of TS-1 zeolite. In catalytic hydroxylation of 2,3,6-trimethylphenol, MTS-5 and MTS-8 show higher activities in comparison with microporous crystal of TS-1 and mesoporous material of Ti-MCM-41. More importantly, MTS-5 assembled from preformed titanosilicate precursors in alkaline media has higher silica condensation degree, compared with MTS-8 synthesized in strongly acidic media. After heating at 550 °C for 4 h, MTS-5 basically remains its catalytic activities in hydroxylation of phenol and 2,3,6-trimethylphenol, indicating its higher stability of Ti species for calcination. In contrast, calcined MTS-8 shows much lower conversion than as-synthesized MTS-8.