Abstract:This study aimed to prepare chromium-based catalysts on titanium-modified MCM-41 for oxidative dehydrogenation reactions. MCM-41 was synthesized hydrothermally. In order to increase the hydrothermal stability of support, titanium was added to the MCM-41. The titanium source (K2TiF6) was dissolved in two different solvents (hot water and sulfuric acid). The hydrothermal stability test was performed with the samples. The samples were characterized by XRD, N2 adsorption/desorption, FT-IR, and SEM/EDS analysis. When titanium was added to the MCM-41 structure, it was determined that the pore walls thickened, and the main peak characterizing the hexagonal structure was preserved. With the modification, the average pore diameter of MCM-41 decreased from 28Å to 22Å, and the surface area decreased from 1250 m2/g to 500 m2/g. The hydrothermal stability test indicated that the loading of titanium improved the stability of MCM-41. FT-IR results showed that titanium has formed strong bonds with oxygen atoms, creating Si-O-Ti, Ti-OH, and Ti-O bonds. These bonds enhanced to stabilize the MCM-41 structure, making it more resistant to structural changes. Smaller crystal size (178Å) and higher surface area (554 m2/g) were determined in the support prepared by dissolving the titanium source in hot water. Therefore, this support was used in catalyst synthesis. Chromium-based catalysts on titanium-modified MCM-41 were prepared by wet impregnation method at different chromium loading (3% and 10%, by mass). The presence of the anatase phase of TiO2 and inactive α-Cr2O3 in the high chromium-loaded sample was determined. Therefore, catalytic tests were carried out with a catalyst containing 3% chromium by mass, prepared using a Ti-modified support, as well as a catalyst prepared using an unmodified support. The highest isobutane conversion (94%) and isobutene selectivity (81%) values were obtained for catalyst supported on Ti-modified MCM-41. High activity predicted for catalyst supported on modified MCM-41 was explained by improving hydrophilic properties.

Catalytic Activity of Ti-Modified MCM-41 for Oxidation of Secondary Alcohol with H2O2

Selective Aerobic Oxidation of Aromatic Alcohols Catalyzed by Tio(2): an Insight on the Effect of Surface Fluorination

The catalytic reactivity of titanium dioxide supported on SBA-15 catalyst for selective oxidation of benzyl alcohol

Ionic Liquid Dispersed Ti/SBA-15 for Double-Bond Cleavage Oxidation of Α-Methylstyrene into Acetophenone

Oxidation of Aliphatic Alcohols by Using Precious Metals Supported on Hydrotalcite under Solvent- and Base-Free Conditions

SYNTHESIS AND CHARACTERIZATION OF CHROMIUM-BASED CATALYSTS ON TITANIUM-MODIFIED-MCM-41 FOR OXIDATIVE DEHYDROGENATION OF ISOBUTANE

Synthesis and characterization of TiO2-V2O5-MCM-41 for catalyzing transesterification of dimethyl carbonate with phenol

Phosphotungstic Acid Supported on MgAl2O4 Nanoparticles as an Efficient and Reusable Nanocatalyst for Benzylic Alcohols Oxidation with Hydrogen Peroxide

RKCL3827 METHANOL SYNTHESIS BY CO2 HYDROGENATION OVER TITANIUM MODIFIED Γ-Al2o3 SUPPORTED COPPER CATALYSTS

Hierarchically Porous Hydrothermal Carbon Microspheres Supported N-Hydroxyphthalimide As a Green and Recyclable Catalyst for Selective Aerobic Oxidation of Alcohols.

In Situ Hydrogen Peroxide Production for Selective Oxidation of Benzyl Alcohol over a Pd@Hierarchical Titanium Silicalite Catalyst

Ti incorporation in MCM-41 mesoporous molecular sieves using hydrothermal synthesis

Solvent-free selective oxidation of alcohols with tert-butyl hydroperoxide catalyzed by palladium(II) isatin Schiff base complex supported into three-dimensional mesoporous silica KIT-6

Mesoporous Polyoxometalate-Based Ionic Hybrid As A Triphasic Catalyst for Oxidation of Benzyl Alcohol with H2o2 on Water

Photothermal dependence on catalytic activity and selectivity of HMF and benzyl alcohol oxidation over Pd/1D‐TiO2 nanotubes

Preparation of Mesoporous Silica Nanostructure Functionalized With Hydrobenzoin Substituted Phthalocyanine and Its Catalytic Performance in Benzyl Alcohol Oxidation

Titanium-containing mesoporous molecular sieves for catalytic oxidation of aromatic compounds

Palladium-doped hierarchical ZSM-5 for catalytic selective oxidation of allylic and benzylic alcohols

Aqueous acidic hydrogen peroxide as an efficient medium for tungsten insertion into MCM-41 mesoporous molecular sieves with high metal dispersion

Preparation of Mesoporous Supported CuCo2O4 Catalyst and Selective Oxidation of Benzyl Alcohol

Preparation and catalytic performance of the supported Ti-MWW zeolites