Pitting corrosion induced by the interaction between microstructures of iron-based alloy in chloride-containing solution

Weishan Li,Jingli Luo
DOI: https://doi.org/10.1023/A:1016516318050
2002-01-01
Journal of Materials Science Letters
Abstract:Success in our modern industrial technology depends to a great extent on the application of metals. Iron-based alloys are widely used in industry due to their excellent strength, good mechinability and good weldability, especially due to their low cost. However, the industrial equipments made from iron-based alloys need for protection from corrosion, because iron is active in many environments. One important way to protect iron-based alloys from corrosion is to form a passive film on the alloys with oxidants or by anodic polarization if the alloys can be passivated in the environments. Unfortunately, pitting corrosion might occur on the passivated metal due to local weakness of the passive film and might cause catastrophe because its initiation is difficult to be predicted. Understanding more about pitting initiation is necessary for the best application of iron-based alloys. Many mechanisms have been proposed to explain pitting corrosion of metals [1‐10]. However, little work has been reported about the difference of pitting susceptibility between microstructures of iron-based alloys. An alloy with micro-alloyed elements and with 0.43‐0.47% carbon content has been widely used for pipeline to transport different media such as water, oil and their mixtures. This alloy has a hypoeutectoid base microstructure, which inevitably contains other microstructures such as ferrite and martensite due to the working process. In practice, pitting usually occurs favorably on some microstructure. The purpose of this paper is to understand the pitting mechanism of a hypoeutectoid iron-based alloy with inclusion of martensite by studying electronic properties of hypoeutectoid and martensite electrodes and their interaction in nitrite solution with or without chloride ions. All specimens were made from an iron-based alloy with compositions of 0.47 wt% C, 1.20 wt% Mn, 0.15 wt% Si, 0.05 wt% P, 0.06 wt% S, 0.40 wt% Cu, 0.40 wt% Ni, 0.15 wt% Mo, and 0.19 wt% V. To determine the metallographic microstructures, specimens were polished with 0.05 µ mA l 2O3, then etched with 0.2% HNO3 ethanol solution and observed under a microscope. Based on the observation under the microscope, hypoeutectoid and martensite areas were determined and cut to make hypoeutectoid and martensite electrodes used for electrochemical measurements. The ∗ Author to whom all correspondence should be addressed.
What problem does this paper attempt to address?