Controlling the Heterocoagulation Process for Fabricating PS–CoFe2O4 Nanocomposite Particles

Yunxing Li,Dongping Yin,Zhaoqun Wang,Bing Li,Gi Xue

DOI: https://doi.org/10.1016/j.colsurfa.2009.02.001

2009-01-01

Abstract:Most ordinary polystyrene (PS) microspheres without any surface modification and hard magnetic cobalt ferrite (CoFe2O4) nanoparticles were, respectively, used as large host particles and small guest particles in a heterocoagulation system. In order to achieve a regular heterocoagulation for fabricating PS–CoFe2O4 composite particles having tailored morphology, chief attention was focused on controlling over the heterocoagulation process instead of the surface modification of the polymer microspheres. A process was adopted, which included blending the two colloids at pH 1 and then, adjusting the pH value of the blending colloid to an optimal range of 2–4 under a suitable weight ratio of the two kinds of particles. The results of TEM, SEM, ζ-potential, TGA and magnetization measurements have confirmed the high density of coverage of the CoFe2O4 nanoparticles onto the surface of polystyrene particles.