Abstract:The crystallization process of β zeolite has been investigated by using FT-IR, XRD, TG, SEM, and ICP-AES. The samples were obtained by hydrothermal synthesis at 140 °C and chemical composition of the mixture used for synthesis can be expressed as n(Al2O3) : n(SiO2) : n(TEABr) : n (Na2O) : n(NaF) : n(H2O) : n [(NH4)2O] = 1 : 25 : 7. 5 : 2. 5 : 3. 75 : 550 : 6. 25. The crystallization curve of zeolite β exhibits a typical S-shaped characteristic. The typical framework IR-absorptions at 567 and 518 cm-1 have different natures. The former is detected at the beginning of induction period and its intensity changes a little in induction period, but exhibits a direct correlation with crystallinity in growth period. The latter is not detected in the induction period, but exhibits the same trend in growth period. The large amorphous SiO2-Al2O3 particles which are visible at the beginning of crystallization change into small grains during the induction period. n(SiO2)/n(Al2O3) ratio of the solid phases obtained at different synthesis time changes significantly during the induction period, but changes a little in growth period. So the β zeolite crystal nucleus are formed via liquid-phase synthesis mechanism. A typical gel in synthesis of β zeolite is transformed initially into a solid, which contains richer aluminium, minor F- and occluded TEA species. The aluminosilicate gel particles are dissolved by F- during the induction period and the transition complex, which has a specific weak X-ray diffraction peak at 2θ = 22. 8° and specific DTG pattern, is formed at the turning point from induction period to growth period. During the growth period Si and Al transport from the liquid to the solid phase at almost the same rates. F- anion has greater influence on the formation and turning of transition complex.

Synthesis and structure of polymorph B of Beta zeolite

Synthesis and Structure of Polymorph B of Zeolite Beta

Studies on the Stacking Fault Structure in Zeolite Beta

Intergrown New Zeolite Beta Polymorphs with Interconnected 12-Ring Channels Solved by Combining Electron Crystallography and Single-Crystal X-ray Diffraction

SSZ-87: a Borosilicate Zeolite with Unusually Flexible 10-Ring Pore Openings.

Highly Mesoporous Single-Crystalline Zeolite Beta Synthesized Using a Nonsurfactant Cationic Polymer As a Dual-Function Template.

Zeolite structure determination using electron crystallography

Synthesis, Surface and Crystal Structure Investigation of the Large Zeolite Beta Crystal

Non-framework Cation Locations in Zeolite Beta

Incorporation of titanium into polymorph C of zeolite beta

Tailoring the structure of hierarchically porous zeolite beta through modified orientated attachment growth in a dry gel system.

Synthesis of all-silica zeolite beta

A surfactant-directed sol-gel evolution in the formation of hierarchical zeolite beta

Al distribution and structural stability of H-BEA zeolites at different Si/Al ratios and temperatures: a first-principles study

Structure Elucidation and Computationally Guided Synthesis of SSZ‐43: A One‐Dimensional 12‐ring Zeolite with Unique Sinusoidal Channels

Synthesis of small crystal zeolite beta in a biphasic H2O–CTAB–alcohol system

Synthesis of β Zeolite Using Tetraethylammonium Bromide Together with Fluoride as Composite of Template (II) - Studies on Crystallization Process of β Zeolite

Stable, Porous, and Bulky Particles with High External Surface and Large Pore Volume from Self-assembly of Zeolite Nanocrystals with Cationic Polymer

Synthesis of Highly Crystalline Beta/MCM-41 Composites by Controllable Assembly of Tailorable Nano Proto-Zeolitic Building Blocks

Enhanced acidity and hydrothermal stability of mesoporous aluminosilicate with secondary building units characteristic of zeolite Beta

Hierarchical Mesoporous Zeolites with Controllable Mesoporosity Templated from Cationic Polymers