Abstract:Mesoporous core-shell composites with large-pore silica shells are highly desired for a broad spectrum of applications. We report an ultra-dilute liquid-phase coating strategy in an acidic medium for controllable synthesis of uniform micro/mesoporous core-shell composites zeolite@SBA-15 comprising zeolite cores and mesoporous silica SBA-15 shells using triblock compolymer Plunoric P123 as a template. Structural characterizations show that the core-shell composites possess tunable specific surface areas (115-228 m(2) g(-1)), large pores (similar to 7.0 nm in diameter) with plenty of mesotunnels (similar to 3.0 nm) from silica shells, original crystalline zeolite frameworks, and opened junctions between micropores and mesopores. The silica shells have ordered 2-D hexagonal mesopore channels, most of which are annularly parallel (fingerprint-like arrangement) to the anisotropic zeolite faces. The shell-thickness is crystal face-dependent, which could be facilely tuned in the range of 30-45 and 40-120 nm on a pinacoids/dome faces and b pinacoids of a zeolite single-crystal, respectively. Moreover, the synthesis parameters such as MgSO4 additive, stirring rate, acidity, temperature and reaction time show great influences on the formation of uniform core-shell composites. Post-hydrothermal treatment at 100 degrees C has been for the first time adopted to improve mesostructural regularity of the core-shell composites. A scheme regarding surface-induced micellization and hydrothermal rearrangement of mesostructured silica shells in the coating process is proposed to illustrate the formation of core-shell composites. The core-shell composite HZSM-5@SBA-15 (HZ@S15) was employed as a catalyst for methanol to propylene (MTP) conversion, and shows excellent catalytic performance with high methanol conversion (similar to 98%) and propylene to ethylene (P/E) ratio (similar to 10.7) as well as propylene selectivity (similar to 39%).

Synthesis of Highly Crystalline Beta/MCM-41 Composites by Controllable Assembly of Tailorable Nano Proto-Zeolitic Building Blocks

Synthesis, Characterization, and Catalytic Properties of A Hydrothermally Stable Beta/Mcm-41 Composite from Well-Crystallized Zeolite Beta

Synthesis and characterization of MCM-49/ZSM-35 composite zeolites in the hexamethyleneimine and cyclohexamine system

A Novel Approach To Prepare Beta-Zeolite/Mcm-41 Composite Molecular Sieve With High Hydrothermal Stability

Synthesis of small crystal zeolite beta in a biphasic H2O–CTAB–alcohol system

Controllable synthesis of hierarchical beta nanozeolites from tailorable seeds

Rapid hydrothermal synthesis of hierarchical ZSM-5/beta composite zeolites

Self-Assembly of Cetyltrimethylammonium Bromide and Lamellar Zeolite Precursor for the Preparation of Hierarchical Mww Zeolite

Tailoring the structure of hierarchically porous zeolite beta through modified orientated attachment growth in a dry gel system.

Highly Mesoporous Single-Crystalline Zeolite Beta Synthesized Using a Nonsurfactant Cationic Polymer As a Dual-Function Template.

A surfactant-directed sol-gel evolution in the formation of hierarchical zeolite beta

Shape-controlled Synthesis of Monolithic ZSM-5 Zeolite with Hierarchical Structure and Mechanical Stability

Cooperative Surface Passivation and Hierarchical Structuring of Zeolite Beta Catalysts

CTAB Resulted Direct Synthesis and Properties of Hierarchical ZSM-11/5 Composite Zeolite in the Absence of Template

Controllable Fabrication of Uniform Core–shell Structured Zeolite@sba-15 Composites

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

Synthesis, characterization, and catalytic application of hierarchical nano-ZSM-5 zeolite

Ultrafast synthesis of high-silica Beta zeolite from dealuminated MOR by interzeolite transformation for methanol to propylene reactions

Templated Synthesis of Hierarchically Mesoporous Zeolites from Cationic Polymers and Their Excellent Catalytic Properties

Mesoscale Reorganization of the Depolymerized Aluminosilicate into Single-Crystalline Hierarchical Zeolite

Rational Manipulation of Stacking Arrangements in Three‐Dimensional Zeolites Built from Two‐Dimensional Zeolitic Nanosheets