Microstructure and Compositional Distribution in an Nb-Ti-Si-Cr-Hf-Al-B-Y Ultrahigh Temperature Alloy Ingot Prepared by Arc Melting

YAO Cheng-fang,GUO Xi-ping,GUO Hai-sheng,LI Yong-kai

DOI: https://doi.org/10.3969/j.issn.1001-4381.2007.z1.038

2007-01-01

Journal of Materials Engineering

Abstract:A master alloy ingot of Nb-Ti-Si-Cr-Hf-Al-B-Y ultrahigh temperature alloy was prepared by firstly vacuum non-consumable arc melting and then vacuum consumable arc melting.The microstructure and compositional distribution in the master alloy ingot was analyzed.It has been found that the microstructure of the ingot was mainly composed of Nbss(Nb solid solution) and(Nb,X)5Si3(where X represents Ti,Hf and Cr elements) phases.The microstructure on the edge of the ingot was mostly consisted of Nbss+(Nb,X)5Si3 eutectic colonies,but there was very small amount of primary Nbss dendrites at some local places.However,the microstructure was composed of big primary(Nb,X)5Si3 blocks or plates and Nbss+(Nb,X)5Si3 eutectic colonies in the central part of the ingot.The compositional distribution was not uniform in the master alloy ingot. The Si content increased from the edge part to the central part of the ingot,but decreased from the lower part to the upper part of the ingot.The Ti content was decreasing both from the edge part to the central part and from the lower part to the upper part of the ingot.