PREPARATION AND CHARACTERIZATION OF CROSS-LINKED PVC/TPU LIGHTWEIGHT MATERIALS

Lei Jiao,Cong Chen,Cheng Chen,Wei-hong Guo,Ji-kui Wang

DOI: https://doi.org/10.3724/SP.J.1105.2012.12001

2012-01-01

Acta Polymerica Sinica

Abstract:A lightweight material based on PVC/TPU blend was studied,which was prepared by incorporation of DCP as cross-linking agent,AC forming agent,hollow glass microsphere and other accessory ingredients via melt blending,and foam materials were prepared via molding method.The effects of the composition ratio of PVC/TPU,DCP content and hollow glass microsphere content on the properties of PVC/TPU lightweight materials were investigated by the density,impact,tensile and flexible test.FTIR analysis showed that groups of materials were changed in modified material.Bubble quality,size and the topology were studied by SEM.Polyester TPU modified the impact and flexible strength,the lowest density was 0.30 g/cm3,as TPU content was 10 phr.With addition of DCP content the lightweight material density declined first and then increased.The results observed by FTIR and gel content test indicated that cross-linking network formed in PVC/TPU lightweight materials.Addition of hollow glass microspheres made the density and mechanical properties of PVC/TPU light material improved obviously,but density was still less than 1.0 g/cm3.SEM showed that the bubbles were intact,hardly be broken and bubble walls were thickened with addition of DCP.Hollow glass microspheres were distributed in the bubble wall,which could cause foam and support more strength.