Abstract:A novel bio-based benzoxazine resin (phenolphthalein-furfuramine-benzoxazine , PTL-F-BOZ) , used bio-based furfurylamine , phenolphthalein , and paraformaldehyde as raw materials , was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR) , nuclear magnetic resonance (H-1 NMR and C-13 NMR) . The curing , thermal and flame retardant properties were analyzed by differential scanning calorimetric (DSC) , thermogravimetric analyzer (TG) , limiting oxygen index (LOI) , vertical burning test, microscale combustion calorimetry (MCC) , cone calorimeter(Cone) and scanning electron microscope (SEM) . The DSC curve of PTL-F-BOZ showed a two-stage curing with two maxima at 224 and 251 degrees C respectively, and had lower curing temperature than that of the traditional fossil-based bisphenol benzoxazine bisphenol A-aniline benzoxazine (bisphenol A-aniline-benzoxazine , BPA-A-BOZ) . The presence of the furan ring in the furfurylamine increased the cross-linking density of polymer, retarded the rearrangement reaction from the phenoxy structure to the phenol structure, and resulted in two curing peaks in the DSC curve of PTL-F-BOZ. Under nitrogen and air atmospheres, the temperatures of 5% mass loss (T-5%) for PPTL-F-BOZ resin were 380 and 370 degrees C , respectively and the residual chars at 800 degrees C were 63. 0% and 10. 5% , respectively. Compared with PBPA-A-BOZ resin, PPTL-F-BOZ resin both possessed higher T-5% and residual char of 800 degrees C. From the DTG curve , the maximum mass loss rates of two decomposition stage (Peak 1 and Peak 2 values) of PPTL-FBOZ resin were 0. 67%/min and 3. 28%/min, which were only 7. 38% and 63. 44% of PBPA-A-BOZ (9. 07%/min and 5. 17%/min) under nitrogen atmosphere , and those were also the same under air atmosphere. LOI of PPTL-F-BOZ resin was 36. 2%, which was higher than that of PBPA-A-BOZ resin. Meanwhile, in the UL-94 test, PPTL-F-BOZ resin extinguished quickly and released less smoke during combustion process, and the original morphology was kept well and a stable carbon layer was formed after burning. Its first ignition time(t(1)) and second ignition time(t(2)) were 1. 4 and 8. 5 s , respectively , far smaller than the maximum permissible values of 10 s, and a UL94 V-0 rating was also achieved. Hence, PPTL-F-BOZ resin showed excellent thermal and flame retardant properties.

Preparation and Characterization of High Char Yield Polybenzoxazine/polyarylacetylene Blends for Resin‐transfer Molding

Synthesis and Properties of a Novel Bio‐based Benzoxazine Resin with Excellent Low‐temperature Curing Ability

Synthesis and Properties of a Novel Bio-based Benzoxazine

Synthesis, Curing, and Thermal Stability of Low-Temperature-Cured Benzoxazine Resins Based on Natural Renewable Resources

Novel Full Bio-Based Phloroglucinol Benzoxazine Resin: Synthesis, Curing Reaction and Thermal Stability

Synthesis of Aromatic Diamine-Based Benzoxazines and Effect of Their Backbone Structure on Thermal and Flammability Properties of Polymers

Preparation, Curing Properties, and Phase Morphology of Epoxy-Novolac Resin/multiepoxy-Terminated Low-Molecular-weight Poly(phenylene Oxide) Blend

Synthesis, characterization, and thermal properties of benzoxazine monomers containing allyl groups

Preparation and Properties of Polybenzoxazine Blends and Their Glass Fabric-Reinforced Composites

An investigation on the effect of phenylboronic acid on the processibilities and thermal properties of bis-benzoxazine resins

Synthesis and Characterization of Acetylene-Terminated Polybenzoxazines Based on Polyaralkyl-Phenolic Prepolymer

Preparation and Curing of Low-viscosity Benzoxazine Resin

Greatly Enhanced Thermo-Oxidative Stability Of Polybenzoxazine Thermoset By Incorporation Of M-Carborane

High Performance Thermosets from a Curable Diels–Alder Polymer Possessing Benzoxazine Groups in the Main Chain

Preparation and properties of silicon-containing arylacetylene resin/benzoxazines blends

Curing behaviour and properties of a novel benzoxazine resin via catalysis of 2-phenyl-1,3,2-benzodioxaborole

Synthesis of triphenol‐diamine‐type hyperbranched benzoxazine and improvement of thermal properties and toughness of typical benzoxazines

Synthesis and Thermal Properties of Polybenzoxazole from Soluble Precursor with Hydroxy-Substituted Polyenaminonitrile

Improvement of aldehyde‐functional polybenzoxazine processability and mechanical properties achieved by 5‐aminoindole/benzoxazine copolymerization

Synthesis and Properties of Highly Cross-Linked Thermosetting Resins of Benzocyclobutene-Functionalized Benzoxazine

An M‐phenylenediamine‐based Benzoxazine with Favorable Processability and Its High‐performance Thermoset