Effects of Nucleating Agent and Nano-Calcium Carbonate on Crystallization Behavior and Mechanical Properties of Polypropylene

HUANG Yi-Ping,ZHANG Yan,CHEN Lei,CHEN Ye,CHEN Guang-Mei

DOI: https://doi.org/10.3969/j.issn.1000-0518.2008.01.015

2008-01-01

Abstract:The nucleating agent 1,3;2,4-di-p-chlorinbenzylidene sorbitol(CDBS) and nano-calcium carbonate(nano-CaCO3) were added in polypropylene(PP).The results of DSC indicate that the crystallization rate and the crystallization temperature of PP increased with the addition of nano-calcium carbonate particles,while the crystallinity of PP did not change obviously.The crystallization temperature of PP with nucleating agent CDBS was higher than that of non-nucleated PP by about 20 ℃.The crystallization rate and the crystallinity of PP increased with the addition of CDBS,with the crystallinity of PP reaching 38%.The results of XRD and PLM show that the nucleating density increased obviously when CDBS was added into the samples.But the crystal structure of the α-form of polypropylene was essentially unaffected by the nucleating agent.CDBS was an effective nucleating agent for PP.The haziness of the sample decreased from 56% to 12% with the addition of CDBS and CDBS was a good transparent agent for PP.The nucleating agent and the nanoparticles could increase the tensile strength and impact strength of PP.The impact strength of PP increased from 33 J/m to about 44 J/m.But CDBS reduced the ultimate strain of the sample by about 26%.