Abstract:TiAlN and AlCrN coatings are widely used in applications that require high stress resistance. In this work, the tribological behaviour of physical vapour deposition (PVD) TiAlN and AlCrN commercial coatings deposited on AISI martensitic stainless steel is studied. Microstructure of the coatings was analysed by X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM) and nanohardness was measured. Pin-on-disk and abrasive wear tests were performed. Adhesion was evaluated using Rockwell C Indentation and scratch test. The thickness of both coatings was approximately 3 μm. AlCrN lost 30 and 10 times less volume than TiAlN in pin-on-disk tests, under low and high loads, respectively. The steady friction coefficient value was also lower. This indicated that the AlCrN coating had a better performance under sliding conditions. On the other hand, the mass loss was similar for both coatings under abrasive wear, even under severe conditions. In the scratch tests, TiAlN coating failed at 60 N load and AlCrN coating at 70 N, the latter showing a higher value of critical load. The deformation was similar for both coatings as it could be observed in the profiles obtained by a mechanical profilometer at 60 N, however, AlCrN did not show film delamination. This enhanced performance can be attributed to higher fracture toughness and load carrying capacity, which not only improved the mechanical properties of the coating but also its adhesion to the stainless-steel substrate.

Evaluation of Tribological Properties of A Cathodic Arc Ion-Plated Crsin Coating under Both Unlubricated and Boundary-Lubricated Conditions

Microstructure and Tribological Properties of Multilayered ZrCrW(C)N Coatings Fabricated by Cathodic Vacuum-Arc Deposition

Friction and wear properties of CrSiCN coatings with low carbon content as sliding against SiC and steel balls in water

Microstructure, Mechanical and Tribological Properties of CrSiC Coatings Sliding Against SiC and Al2O3 Balls in Water

Microstructure, Mechanical, and Tribological Properties of Cr-Ti-Si-N Coatings

Tribological Properties of Cr(Si)CN Coatings Sliding Against Different Mating Balls in Water

A comparative analysis of different surface tribological and electrochemical properties of TiAlN, TiAlSiN, and CrAlN thin film coatings in seawater

Comparisons of tribological and electrochemical properties of CrSiC and CrSiCN coatings in seawater

Friction and Wear Properties of CrSiCN/SiC Tribopairs in Water Lubrication

Tribological Behavior of Various Plasma-Sprayed Ceramic Coatings

Current carrying tribological properties of multi arc ion plated titanium nitride doped silver coating

Effect of Si Content on the Tribological Properties of Crsin Films in Air and Water Environments

Tribological performance of the gradient composite TiAlSiN coating with various friction pairs

Friction and wear performance of electrospark deposited Ni/C-MoS2 self-lubricating coating

ANALYSIS OF THE TRIBOLOGICAL PROPERTIES OF TiN/Si3N4 NANOCOMPOSITE COATING IN SLIDING CONTACT WITH CERAMIC, STEEL, AND POLYMER COUNTERPART

Study on Wear and Friction Resistance of CrTiAlMoN Coatings Deposited by Magnetron Sputtering

Tribological Properties of CrN Coating Deposited on 20crmo Against Tin Bronze

Comparative study on mechanical and tribological properties of Cr–Al–N and Cr–Al–O coatings deposited by cathodic arc evaporation

Tribological performance of Mn3(PO4)2 coating and PC/MoS2 coating in Rolling–Sliding and pure sliding contacts with gear oil

Tribological Properties of Craln and Tin Coatings Tested in Nano- and Micro-Scale Laboratory Wear Tests

Tribological behaviour of TiAlN and AlCrN coatings on stainless steel