Study on Impact Property and Weather Resistance of EPDM-g-MS/PS by Suspension Copolymerization

FU Jin-feng,MAI Jian-zhang,WANG Lian-shi,CAI Tong-min,ZHANG An-qiang,ZENG Xiang-bin,WANG Xia
2010-01-01
Abstract:With ethylene-propylene-diene mischpolymere(EPDM),methyl methacrylate(MMA),and styrene(St)as raw materials,EPDM graft MMA-St copolymers(EPDM-g-MS)synthesized by suspension grafting copolymerization was blended with polystyrene(PS)resin to prepare a EPDM-g-MS/PS(MES)high impact resisitance plastic.The effects of fMMA,weight fraction of MMA in the charge monomers MMA-St,and FMMA,weight fraction of MMA unit in the copolymer formed by MMA-St,on notched impact strength of MES were investigated.The phase structure,toughening mechanism,thermal stability and weathering resistance of MES were studied,and compared with the properties of SBS/PS blends.The results showed that EPDM-g-MS had the best toughening effects on PS resin when fMMA and FMMA was 15% and 29.1% respectively,the notched impact strength of MES containing 30% of EPDM,reached 45.1 kJ/m2.EPDM phase exhibited dispersed phase with concealed structure in microstructure of MES,whose toughening mechanism was branch and termination of crack,accompanying slight shear yielding of matrix.In comparison,1,4-polybutadiene block of SBS exhibited continuous phase in microstructure of SBS/PS blends,and the toughening mechanism of which was shear yielding of matrix.Thermal stability and properties of resistance to yellow discoloration by weathering aging of MES were significantly higher than those of SBS/PS blends.
What problem does this paper attempt to address?