Abstract:Background: The NiTi alloy, known for its shape memory and superelasticity, is increasingly used in medicine. However, its high nickel content requires enhanced biocompatibility for long-term implants. Low-temperature plasma treatments under glow-discharge conditions can improve surface properties without compromising mechanical integrity. Methods: This study explores the surface modification of a NiTi alloy by oxidizing it in low-temperature plasma. We examine the impact of process temperatures and sample preparation (mechanical grinding and polishing) on the structure of the produced titanium oxide layers. Surface properties, including topography, morphology, chemical composition, and bioactivity, were analyzed using TEM, SEM, EDS, and an optical profilometer. Bioactivity was assessed through the deposition of calcium phosphate in simulated body fluid (SBF). Results: The low-temperature plasma oxidization produced titanium dioxide layers (29-55 nm thick) with a predominantly nanocrystalline rutile structure. Layer thickness increased with extended processing time and higher temperatures (up to 390 °C), though the relationship was not linear. Higher temperatures led to thicker layers with more precipitates and inhomogeneities. The oxidized layers showed increased bioactivity after 14 and 30 days in SBF. Conclusions: Low-temperature plasma oxidation produces bioactive titanium oxide layers on NiTi alloys, with a structure and properties that can be tuned through process parameters. This method could enhance the biocompatibility of NiTi alloys for medical implants.

Spark Plasma Sintering of TiNi Nano-Powders for Biological Application

In Vitro and in Vivo Evaluation of Porous NiTi Alloy Modified by Sputtering a Surface TiO2 Film

Spark Plasma Sintering of Pure Titanium: Microstructure and Mechanical Characteristics

Structure and Properties of Bioactive Titanium Dioxide Surface Layers Produced on NiTi Shape Memory Alloy in Low-Temperature Plasma

Preparation and cytocompatibility of Ni-Ti-O nanospindles on NiTi alloy

Nano-Scale Surface Morphology, Wettability and Osteoblast Adhesion on Nitrogen Plasma-Implanted NiTi Shape Memory Alloy

Fabrication of Titanium-Niobium-Zirconium-Tantalium Alloy (TNZT) Bioimplant Components with Controllable Porosity by Spark Plasma Sintering

In Vitro Bioactivity and Osteoblast Response on Chemically Modified Biomedical Porous NiTi Synthesized by Capsule-Free Hot Isostatic Pressing

Surface Characteristics, Mechanical Properties, and Cytocompatibility of Oxygen Plasma-Implanted Porous Nickel Titanium Shape Memory Alloy

Enhanced Bioactivity of Biomedical Niti Through Surface Plasma Polymerization

Preparation of Ni–Ti composite powder using radio frequency plasma spheroidization and its laser powder bed fusion densification

Microstructures and Mechanical Properties of Ti-43Al-5V-4Nb-Y Alloy Consolidated by Spark Plasma Sintering

In Vitro Corrosion and Cytotoxicity on Microcrystalline, Nanocrystalline and Amorphous NiTi Alloy Fabricated by High Pressure Torsion

Ni-free Ti-based Bulk Metallic Glass with Potential for Biomedical Applications Produced by Spark Plasma Sintering

Suppression of Nickel Out-Diffusion from Porous Nickel-Titanium Shape Memory Alloy by Plasma Immersion Ion Implantation

Oxygen and Sodium Plasma-Implanted Nickel–titanium Shape Memory Alloy: A Novel Method to Promote Hydroxyapatite Formation and Suppress Nickel Leaching

Calcium filling of TiO2 nanotubes on the surface of NiTi shape memory alloys by plasma immersion ion implantation

Microstructure and Mechanical Properties of TiN/Si3N4 Nanocomposites by Spark Plasma Sintering (SPS)

TiNi shape memory alloy coated with tungsten: a novel approach for biomedical applications

Spark Plasma Sintering of Titanium Aluminides: A Progress Review on Processing, Structure-Property Relations, Alloy Development and Challenges

Preparation of fine-grains TiAl alloys by mechanical alloying and spark plasma sintering