Abstract:In this study, glycidyl methacrylate was copolymerized with poly(ethylene glycol) methyl ether methacrylate to obtain a copolymer {poly[glycidyl methacrylate-poly(ethylene glycol) methyl ether methacrylate] [P(GMA-PEGMA)]}, which was crosslinked with alpha,omega-diamino poly(propylene oxide) (Jeffamine) at various weight ratios and molecular weights to form novel gel polymer electrolytes (GPEs). The crosslinked copolymers were characterized by Fourier transform infrared spectroscopy and thermal analysis. The crosslinked polymers were amorphous in the pristine state and became crystallized after they were doped with lithium electrolyte. Furthermore, the crosslinking degree of the crosslinked polymers increased with increasing weight ratio of Jeffamine, and both the swelling properties and mechanical behaviors of the crosslinked polymers were heavily affected by the weight ratio and molecular weight of Jeffamine. The ionic conductivity (sigma) of the GPEs from the crosslinked copolymers was determined by alternating-current impedance spectroscopy. A higher molecular weight and increased weight ratio of Jeffamine resulted in a higher sigma. The GPE based on P(GMA-PEGMA) crosslinked with an equal weight of Jeffamine D2000 exhibited the highest sigma of 8.29 x 10(-4) S/cm at 25 degrees C and had a moderate mechanical strength. These crosslinked copolymers could be potential candidates for the construction of rechargeable lithium batteries. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 120: 2979-2984, 2011

Preparation and characterization of a semi-interpenetrating network gel polymer electrolyte

Synthesis and Characterization of Novel Semi‐interpenetrating Polymer Network Electrolyte Based on Crosslinked P(GMA‐co‐AN)/PEO

Preparation and Properties of Gel Membrane Containing Porous PVDF-HFP Matrix and Cross-Linked PEG for Lithium Ion Conduction

Preparation and Characterization of Novel Crosslinked Poly[glycidyl Methacrylate–poly(ethylene Glycol) Methyl Ether Methacrylate] As Gel Polymer Electrolytes

Effects of PDMS with Polyether Side Chains on the Fluoropolymer Based Gel Lithium Electrolytes

Novel Amphiphilic Polymer Gel Electrolytes Based on (Peg-B-gma)-co-mma

Preparation and characterization of a novel microporous PE membrane supporting composite gel polymer electrolyte

Crosslinked poly(acrylonitrile–glycidyl methacrylate) as a novel gel polymer electrolyte

Preparation and Performances of A Novel Gel Polymer Electrolyte

Synthesis and Characterization of Gel Polymer Electrolyte Based on Epoxy Group via Cationic Ring-Open Polymerization for Lithium-Ion Battery

A novel single-ion conductor gel polymer electrolyte prepared by co-irradiation grafting and electrospinning process

Crosslinked Gel Polymer Electrolyte from Trimethylolpropane Triglycidyl Ether by In Situ Polymerization for Lithium-Ion Batteries

Microporous Pvdf-Hfp Based Gel Polymer Electrolytes Reinforced by Pegdma Network

In-situ Crosslinked Gel Polymer Electrolytes Based on Ionic Monomers as Charge Carriers for Lithium-Ion Batteries

Preparation and Characterization of Poly(vinyl Chloride‐co‐vinyl Acetate)‐based Gel Electrolytes for Li‐Ion Batteries

Preparation of Porous, Chemically Cross-Linked, PVdF-based Gel Polymer Electrolytes for Rechargeable Lithium Batteries

Preparation and properties of poly(ethylene oxide) gel filled polypropylene separators and their corresponding gel polymer electrolytes for Li-ion batteries

Macromolecule plasticized interpenetrating structure solid state polymer electrolyte for lithium ion batteries

Preparation and performance of novel acrylonitrile (AN)-based copolymer gel electrolytes for lithium ion batteries

High Strength and Toughness Poly (vinyl alcohol)/Gelatin Double Network Hydrogel Fabricated via Hofmeister Effect for Polymer Electrolyte

In Situ Polymerization Of Methoxy Polyethylene Glycol (350) Monoacrylate And Polyethyleneglycol (200) Dimethacrylate Based Solid-State Polymer Electrolyte For Li-Ion Batteries