Abstract:A commercial mesoporous silica (Grace Davison) was chemically grafted with trimethylsilyl chloride (TMSCl) and hexamethyldisilanaze (HMDS). The silylation process brought about some reduction in the specific BET area, the pore volume, and the pore sizes of the samples. Thermogravimetric studies of the silylated samples revealed that the grafting process is kinetically controlled at short reaction times. In the kinetic regime, increasing concentrations of the silylant agent up to 2 wt% in the solvent led to an increase of the extent of the silylated surface, although this limitation disappeared at higher concentrations. Silylation was confirmed by diffuse reflectance infrared Fourier transform (DRIFTS), (29)Si CP-MAS NMR, and photoelectron (XPS) spectroscopic techniques. Solid-state (29)Si MAS-NMR spectra of the silylated samples revealed the presence of -SiCH(3) groups (9.5 ppm) together with two resonances, Q3 (approximately equal to -104 ppm) and Q4 (approximately equal to -114 ppm), coming from siloxane [Qn approximately Si(OSi)n(OH)(4-n), n approximately 2-4] groups, the Q3 signal decreasing upon silylation. The DRIFT spectra of the silylated samples exhibited two well defined bands at 2970 and 2907 cm(-1), due to stretching vibration modes of the C-H bonds in surface -CH(3) groups formed during the silylation process, and also the disappearance of the band at 3740 cm(-1). This observation indicates the complete removal of terminal and geminal hydroxyl groups by grafting with the silylating agent. Similarly, high-resolution photoelectron spectra of the Si2p core levels showed a high binding-energy component (103.5 eV) in all the samples, coming from the Si coordinated with oxide anions in SiO(2), together with a second component at 102.1 eV, which is the fingerprint of Si coordinated by oxide anions and an organic group. Finally, the samples were ranked according to their hydrophobicity, as determined from the temperature-programmed desorption profiles of adsorbed water and 2-methylbutane.

Distinguishing The Silanol Groups In The Mesoporous Molecular Sieve Mcm-41

Zur Unterscheidung Der Silanolgruppen Im Mesoporösen Molekularsieb MCM‐41

<sup>2</sup>H NMR Studies of Simple Organic Groups Covalently Attached to Ordered Mesoporous Silica

Structural Characteristics Of Mcm-41 Synthesized In-Situ On Silica

Synthesis and properties of mesoporous molecular sieve MCM-41 form extremely dense system

Synthesis and Characterization of the Gallosilicate Mesoporous Molecular Sieve Mcm-41

Synthesis and properties of mesoporous molecular sieve MCM-41 from extreme dense system with auxiliary alkanes

Transformation of Lamellar Silicate into the Mesoporous Molecular Sieve MCM-41

Silylation and surface properties of chemically grafted hydrophobic silica

Preparation of mesoporous Al-MCM-41 with stable tetrahedral aluminum using ionic liquids as a single template

Synthesis of Mesoporous Molecular Sieve Mcm-41 in Extremely Dense System

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

Solid-State Nmr Studies Of The Borosilicate Mesoporous Molecular Sieve Mcm-41

Surface Silylation of Mesoporous Molecular Sieve and Its Hydrophobicity

One- and Two-Dimensional Solid-State Magic Angle Spinning NMR Studies on the Hydration Process of Layered Sodium Disilicate SKS-6

Synthesis and Characterization of AlMCM-41 Molecular Sieves

Synthesis and Characterization of Stable Framework-Iron Containing Mesoporous Molecular Sieves Fe-Mcm-41

Distinguishing Surface Versus Buried Cation Sites in Aluminosilicate Mesoporous Materials

Synthesis of Mesoporous Manganosilicates - Mn-Mcm-41, Mn-Mcm-48 and Mn-Mcm-L

Synthesis and characterization of mesoporous and amorphous silica modified with silica-organo-sulfogroups

Preparation of MCM-41 with high thermal stability and complementary textural porosity