Abstract:Solid-state (1)'H, Na-23, and Si-29 NMR spectroscopies, combined with X-ray powder diffraction (XRD) technique, were used to study the hydration process of a layered sodium disilicate SKS-5 (having a crystal structure of alpha-Na2Si2O5). NMR and XRD experiments suggest that SKS-5 is very sensitive to absorbed water molecules and the crystal structure of SKS-5 converts gradually from alpha-Na2Si2O5 to a new phase during the hydration process. Although the new phase contains about 9% Na2Si4O9, its crystal structure is still unclear. The hydration of SKS-5 begins with the formation of hydrogen-bonded water (with the silicate framework), accompanied by a partial hydrolysis of the Si-O-Si linkages in the framework that generates isolated and hydrogen-bonded silanols (with proton bonded to oxygen atom in the adjacent layer). With an increase of the hydration degree, the above process proceeds and the concentrations of hydrogen-bonded water and hydrogen-bonded silanol increase significantly. When the hydration tune is extended to 6 months, the conversion from SKS-5 to the new phase is accomplished and a new kind of hydrogen-bonded silanols (with the proton bonded to nonbridging oxygen at the same silicon atom) appears. The hydrogen-bonding network formed during the hydration process may probably strengthen the stability of the new phase. The silicon sites in the new phase are confirmed to be mainly Q(2) [(SiO)(2)Si(OH)O-Na-] and Q(3) [(SiO)(3)SiO-Na+] groups. The coordination of sodium ions is also significantly altered after the hydration. The results of Na-23 NMR experiments agree well with the data from H-1 and Si-29 NMR experiments, and five sodium sites with different local environments can be resolved by the Na-23 MAS and two-dimensional Na-23 multiple quantum MAS spectra in different hydration periods. Probably, the hydrolysis of the SKS-5 framework and the variation of the sodium coordination lead to the structural conversion during the hydration process.

One- and Two-Dimensional Solid-State Magic Angle Spinning NMR Studies on the Hydration Process of Layered Sodium Disilicate SKS-6

Stability of Layered Sodium Disilicate during Hydration Process As Studied by Multinuclear Solid State NMR Spectroscopy

Reaction of Layered Sodium Disilicate Sks-6 with Calcium Chloride Solution As Revealed by Solid State Nmr Spectroscopy: Exploring the Calcium Ion Extracting Mechanism of Sks-6

The Dissociated Amorphous Silica Surface: Model Development and Evaluation.

<sup>2</sup>H NMR Studies of Simple Organic Groups Covalently Attached to Ordered Mesoporous Silica

Observation of Silane Coupling Agents Adsorbed on Silica by Solid State 1H NMR under Fast Magic Angle Spinning

In Situ Study of Nanostructure and Morphological Development During the Crystal–mesophase Transition of Poly(di-N-hexylsilane) and Poly(di-N-butylsilane) by X-ray and Hot-Stage AFM

Phase Structure and Transitions in A Poly(Methyloctadecylsilane) Oligomer

Molecular Simulation of the Ions Ultraconfined in the Nanometer-Channel of Calcium Silicate Hydrate: Hydration Mechanism, Dynamic Properties, and Influence on the Cohesive Strength

Transformation of Lamellar Silicate into the Mesoporous Molecular Sieve MCM-41

Calcium and magnesium silicate hydrates formed in the presence of sodium hydroxide: Insight from experiments and DFT simulation

Elucidating the Bimodal Acid-base Behavior of the Water-silica Interface from First Principles

Molecular dynamics study on the Tri-calcium silicate hydration in sodium sulfate solution: Interface structure, dynamics and dissolution mechanism

Structure and vibrational properties of sodium silicate glass surfaces

Role of framework sodium versus local framework structure in determining the hydrothermal stability of MCM-41 mesostructures

Silylation of Mechanically Ground Kaolinite

Dependence of Silica Sol Properties on Synthesis Situation Studied by Saxs

Hydration Properties and Interlayer Organization in Synthetic C-S-H

1H NMR Study of Hydroxy Groups in Mesoporous Molecular Sieve SBA-15

Solid-state NMR Characterization of Β-Sialons from Self-Propagating High-Temperature Synthesis