STUDY ON THE NON-LIQUID-PHASE COORDINATION CROSSLINKING REACTION OF ACRYLONITRILE-BUTADIENE RUBBER/COPPER SULFATE COMPOSITES
Mou Haiyan,Shen Fei,Cao Yuanyi,Yuan Xiaofang,Wu Chifei
DOI: https://doi.org/10.3724/sp.j.1105.2008.00910
2008-01-01
Acta Polymerica Sinica
Abstract:The non-liquid-phase coordination crosslinking reaction of acrylonitrile-butadiene rubber/copper sulfate (NBR/CuSO4) mixture was investigated by differential scanning calorimetry (DSC), Fourier transform infrared (FT-IR) spectrometry and X-ray photoelectron spectroscopy (XPS) The NBR/CuSO4 mixture specimens for DSC and FT-IR were prepared in an open two-roll mill at room temperature by blending NBR ( 100 phr) and CuSO4 powders ( 10,20 and 30 phr, respectively) Specimens for XPS test were prepared by molding NBR/CuSO4 mixtures at 120, 170, 190 and 200 degrees C for 20 min. DSC results showed that pure NBR was thermostable and inert between 150 degrees C and 270 degrees C, while the curves of NBR/CuSO4 mixtures presented three thermopositive peaks in the temperature range from 150 degrees C to 330 degrees C. FT-IR spectrometry indicated that the polymer structure of the specimens maintained without noticeable alteration at temperatures below 200 degrees C. It means there were no oxidations or other exothermal reactions except for the probable coordination reaction between -CN and Cu2+. N1s XPS spectrum of NBR/CuSO4 mixtures Only displayed a single peak with a binding energy of 399.1 eV belonging to free -CN at lower temperature (120 degrees C), while fitting N1s spectrum gave two secondary peaks tit 399.2 eV and 401. 3 eV at the test temperature of 170 degrees C 190 degrees C and 200 degrees C, and the latter was attributed to coordinated -CN. It bore Out that the coordination reaction of -CN and Cu2+ carried out well and truly. Moreover, it was confirmed that the first thermopositive peak of DSC was attributed to the coordination crosslinking reaction of -CN and Cu2+ in the non-liquid-phase mixture. The apparent activation energy and reaction order of the non-liquid-phase coordination crosslinking reaction were evaluated by Kissinger method and Crane equation. With CuSO4 content of 10, 20 and 30 phr the results of apparent activation energy were 86.22, 85.89 and 83.98 W/mol, and the reaction orders were around 0.9.