Effect of Minor Cr Additions on Microstructure and Mechanical Properties of 93W-Ni-fe Alloys

刘文胜,唐芳,马运柱,黄伯云

DOI: https://doi.org/10.3321/j.issn:1004-0609.2008.09.013

2008-01-01

Abstract:The effects of solid solution quenching and element chromium additions on the properties and microstructure of 93W-4.9Ni-2.1Fe alloy were investigated deeply. Optics microsccopy(OM), scanning electricity microsccopy(SEM) and EDAX energy spectrum were used to study the microstructure and compositions of the alloys, respectively. The strength and elongation of alloys were tested with quasi-static tensile testing machine, and the relative densities of the alloys were measured by Archimedes method. The results indicate that when the Cr content (mass fraction) increases from 0 to 1.5%, the tensile strength, relative density and elongation of 93W-Ni-Fe alloy reduce from 997.2 MPa, 99.27% and 14.94% to 834.7 MPa, 95.21% and 5.69%, respectively. Meanwhile, with the Cr content increases from 0 to 1.5%, the tensile strength, relative density and elongation of solid solution quenching 93W-Ni-Fe alloy reduce from 1 039 MPa, 99.33% and 18.37% to 888.5 MPa, 96.10% and 7.39%, respectively. Elements Cr, W, Ni, Fe and O form Cr-rich solid solutions and gather along the interfaces of the alloys, which result in reducing the mechanical properties of 93W-Ni-Fe alloys.