Abstract:The phase equilibria in the Zr–ZrCo–ZrNi system at subsolidus temperature and at 900 and 800°C were first studied using physicochemical analysis methods, and solidus surfaces and isothermal sections at 900 and 800°C were constructed. Isomorphic Zr2Co and Zr2Ni compounds with a tetragonal crystal structure of AlCu2 (θ) type form a continuous series of solid solutions dividing the Zr–ZrCo–ZrNi system into two subsystems: Zr–Zr2Co–Zr2Ni and ZrCo–ZrNi–Zr2Ni–Zr2Co. The equilibria on the solidus surface of the Zr–Zr2Co–ZrCo–Zr2Ni system and at 900°C differ significantly. This is associated with the Zr3Co-based η phase formed by peritectoid reaction 〈β − Zr〉 + 〈Zr2Co〉 → η at 980°C, being close to theL ↔ θ + β eutectic crystallization temperature (986°C), in the binary Zr–Co system. At 900 and 800°C, the 𝜂 phase dissolves up to 14.5% Ni. The solidus surface of the ternary Zr2Co–Zr2Ni–ZrCo–ZrNi system shows a three-phase equilibrium of the θ phase with the ZrCo (δ) and ZrNi (δ2) phases of the ZrCo–ZrNi quasibinary section: δ + δ2 + θ. The plane of this tie-line triangle extends significantly at 900 and 800°C as the solubility of nickel in the cubic ZrCo-based phase of CsCl type changes. At room temperature, all alloys of the ZrCo–ZrNi–Zr2Ni–Zr2Co subsystem should contain three phases: δ + δ2 + θ. The solidus surface of the Zr–ZrCo ZrNi system is thus completed by surfaces corresponding to the homogeneity regions of the δ, δ2, δ, and β phases, θ + δ + δ2 tie-line triangle plane, and ruled surfaces representing the upper boundary of the two-phase θ + δ2, θ + δ, and θ + δ volumes. At 900 and 800°C, two three-phase equilibria, η + θ + β and δ + δ2 + θ, are observed in the system.

Experimental Determination and Thermodynamic Assessment of the Phase Diagram in the Co–Zr System

Ab Initio Calculations of the Thermodynamics and Phase Diagram of Zirconium

Thermodynamic Calculation of Phase Equilibria in the C-Mo-Zr System

Experimental Study on Phase Relationships in the Co-rich Portion of the Co–Ti–Zr System

Experimental Investigation and Thermodynamic Assessment of the Mo–Ni–Zr Ternary System

Experimental determination of phase diagram in the Zn-Fe binary system

Phase diagram, thermodynamic modeling and predictions of glass-forming range and ability in the Co–Cu–Zr system

Experimental determination and thermodynamic calculation of phase equilibria in Ag-Zr-Y system

Phase equilibria thermodynamics and solidified microstructure in the Ag-Cr-Zr system

Thermodynamic Modeling of the B-Ti-Zr System over the Whole Composition and Temperature Ranges

A study on the phase diagram of Re -Zr refractory system

The Co–Ni–Zr Phase Diagram in the Zr–ZrCo–ZrNi Region I. Phase Equilibria in the Zr–ZrCo–ZrNi System at Subsolidus Temperature, 900°C, and 800°C

Phase equilibria in the ZrO 2 –Ta 2 O 5 –Nb 2 O 5 system: Experimental studies and thermodynamic modeling

Thermodynamic Evaluation of the Fe-Zn Binary System with Reference to the Latest Experimental Phase Diagram

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Experimental Investigation of the Co-Ge Phase Diagram

Experimental Constraints on the Phase Diagram of Elemental Zirconium

First-principles calculations, experimental study, and thermodynamic modeling of the Al-Co-Cr system

Measurement of the phase equilibria in the Al–Zr–Y system at 673 and 823 K

Phase Relationships in the Al-rich Region of the Al-Y-Zr System

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C