Abstract:In a typical FCCVD process, the purity of the initial product grown by the standard process was more than 90 wt%, with a yield of 0.5 g/h. The average G/D ratio of the initial product was 178, and it had a distinct RBM peak. HRTEM confirmed that the synthesized SWCNTs had high purity and crystallinity. Carbon nanotubes (CNTs) were synthesized by floating catalyst chemical vapor deposition (FCCVD) reactions. The complicated processing parameters that included a precursor solution composition, reaction temperature, flow rate of the carrier gas, weak oxidants, and injection rate of the precursor solution were controlled to synthesize single‐walled carbon nanotubes (SWCNTs) during the reaction process. The effects of the processing parameters were analyzed with respect to the formation of SWCNTs, yield, and the crystallinity in the CNTs structure. The SWCNTs were characterized by the Raman spectroscopy, scanning electron microscope, high‐resolution transmission electron microscopy, and thermogravimetric analysis. A high reaction temperature, high H2 flow rate, low injection rate of solution precursor, and low concentrations of iron catalysts in the reaction were important factors to improve the crystalline quality of the SWCNTs. The purity of the initial product grown by the standard process was more than 90 wt %, with a yield of 0.5 g/h. The average G/D ratio of the initial product was 178, and it had a distinct RBM peak. HRTEM confirmed that the synthesized SWCNTs had high purity and crystallinity. The SWCNTs could be tunable to meet a particular application by varying the reaction conditions.

Highly Selective Synthesis of Single-Walled Carbon Nanotubes from Methane in a Coupled Downer-turbulent Fluidized-Bed Reactor

Synthesis of High‐Quality, Double‐Walled Carbon Nanotubes in a Fluidized Bed Reactor

Selective Synthesis Combined with Chemical Separation of Single-Walled Carbon Nanotubes for Chirality Selection

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Production of High Quality Single-Walled Carbon Nanotubes in a Nano-Agglomerated Fluidized Bed Reactor

On-line intermittent growth of carbon nanotubes in a self-made tapered fluidized bed reactor at different inlet distances

Synthesis of Single-Walled Carbon Nanotubes by Chemical Vapor Deposition of Methane in A Fluidized Bed Reactor: Temperature and Reaction Time Effects

FEW WALLED CARBON NANOTUBE PRODUCTION IN LARGE-SCALE BY NANO-AGGLOMERATE FLUIDIZED-BED PROCESS

Controllable bulk growth of few-layer graphene/single-walled carbon nanotube hybrids containing Fe@C nanoparticles in a fluidized bed reactor

Selective Synthesis of Single/Double/Multi-walled Carbon Nanotubes on MgO-Supported Fe Catalyst

Very High-Quality Single-Walled Carbon Nanotubes Grown Using a Structured and Tunable Porous Fe/MgO Catalyst

Controlling the Crystalline Quality and Yield of Single‐Walled Carbon Nanotubes via Floating Catalyst Chemical Vapor Deposition Synthesis

Scalable growth of single-walled carbon nanotubes with a highly uniform structure

Producing cleaner double-walled carbon nanotubes in a floating catalyst system

Carburization of Fe/Ni Catalyst for Efficient Growth of Single-Walled Carbon Nanotubes

Synthesis of Single-Walled Carbon Nanotubes by the Vertical Floating Catalyst Method

The Mass Production of Carbon Nanotubes Using a Nano-Agglomerate Fluidized Bed Reactor: A Multiscale Space–time Analysis

Design and Experimental Study of a Tapered Fluidized Bed Reactor without a distributor of Carbon Nanotubes

Enhanced Production of Carbon Nanotubes: Combination of Catalyst Reduction and Methane Decomposition

Catalyst Design Using Nanoporous Iron for the Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes

Production of Carbon Nanotubes in A Packed Bed and A Fluidized Bed