Abstract:In order to illustrate the role of alkali treatment of bamboo particles reinforced polyvinylchloride composites (BPPC), bamboo particles were treated by alkali aqueous solution with a serial concentration of 0.5%, 1%, 2%, 5% and 10%. Mechanical, thermal properties of alkali treated BPPC and micro-micrographs of the fracture surface were researched and compared with raw bamboo particles fabricated BPPC respectively. Results showed that tensile strength of BPPC increased before the solution reached the concentration of 5% and got a maximum value of 15.07MPa at the concentration of 5%. The curve decreased significantly as the concentration of solution went higher as to 10%. Modules of rupture got a highest value of 44.73MPa till reached the concentration of 2% and then decreased. Modules of elasticity increased in the whole before reached the concentration of 5% and the maximum value was 4362.48MPa which was 5 times more than the original bamboo particles. DSC curves illustrated that raw bamboo particles mixed with PVC showed a higher Tg which meant that raw fiber was not well compatible with PVC and BPPC treated with alkali solution performed a better compatibility. According to SEM observations, interface interaction of fiber-matrix that were modified of alkali solution upon bamboo particles appeared a better interlock action correlated to higher mechanical properties and better compatibility between fiber and matrix. Hence, the use of alkali treated bamboo particles as reinforcement was a feasible and competitive method of creating new materials.

Preparation and properties of modified inorganic clay/PVC composites

Modification of inorganic clay and its application in rigid PVC

Role of Alkali Treatment on Mechanical and Thermal Properties of Bamboo Particles Reinforced Polyvinylchloride Composites

Impact of Chemical Modification of Bamboo Fibers on Properties of Fiber Reinforced PVC Composites

Preparation and characterization of organic modified montmorillonite/polylactic acid nanocomposites

Effect of Different Clay Treatment on Morphology and Mechanical Properties of PVC-clay Nanocomposites

Influences of Adding Polymerizable Nonionic Borate Esters/methyl Methacrylate/nano-Caco3 Composites During Polymerization on the Mechanical Properties of PVC Resins

STUDY ON THE MECHANICAL PROPERTIES AND APPLICATION OF PVC/HYPER FINE CaCO3 COMPOSITES IN INJECTION MOLDING

Study on the property of PVC modified by MBS/inorganic material composite

Influences of individual and composed poly(vinyl alcohol) suspending agents on particle morphology of suspension poly(vinyl chloride) resin

The Application of Modified Superfine Ground Calcium Carbonate in Rigid PVC

Morphology and mechanical properties of poly(vinyl chloride)/nano-hydrotalcite composites

Studies on the Structure and Properties of PVC/organic Montmorillonite Composites Toughened by Rigid Inorganic Particles

Effects of Physical Crosslinking on Properties of Plasticized High Molecular Weight PVC

Structure-property relationships of lightly chemical crosslinked poly(vinyl chloride) thermoplastic elastomer

Preparation And Characterization Of Poly(Vinyl Chloride)/Layered Double Hydroxides Nanocomposite Via In Situ Suspension Polymerization

Mechanical Properties of PVC/CPE/CaCO_3 Composites

Effect of Properties of CaCO3 Nanoparticles on Interface and Properties of Poly(vinyl Chloride) Composites

Study on CaCO3/PVC nanocomposite

Studies On Characterization, Thermal Property And Rheological Property Of P(An/Vac)/Clay Nanocomposites

Clay-reinforced PVC composites and nanocomposites