Abstract:Nanosilica particles well dispersed in ethanol were modified by 3-(trimethoxysilyl) propyl methacrylate (MPS) and then re-dispersed into methyl methacrylate (MMA) and poly(methyl methacrylate) matrix via a media replacement process and an in situ bulk polymerization process, respectively. The MPS modified status of silica particles and its effects on the dispersion of silica particles in different media and polymer matrix were systematically investigated by FTIR, TG, DLS and TEM. It was found MPS oligomer was the main form for MPS coupling on silica particles surface. Excessive MPS dosage not only resulted in the formation of MPS homo-polymeric particles in media phase, but also the MPS oligomer thick layer on silica surface, which would inevitably induce the small-scale aggregation of silica particles. There existed an appropriate MPS coupling amount for excellent silica dispersity, which is mainly related with the apparent coupling density of MPS molecules on silica particles surface. When the apparent coupling density is 1. 3 similar to 5. 6 mu mol . (m(2) . SiO2)(-1), the MPS coupling efficiency is acceptable and the modification of silica particles is sufficient. Only on this state, silica particles can be dispersed in the monomer and polymer matrix at the primary particles size level, even in the case of 20% silica content. The silica/monomer dispersion prepared via the above processes exhibited high silica dispersity, high silica content, high storage stability and high grafting controllability on silica surface. All of them imply that this kind of dispersion is avail to prepare silica/PMMA composite microspheres via in situ heterogeneous polymerization, and these microspheres would possess controllable morphology and controllable graft interface.

Surface‐modified Silica Nanoparticles for Reinforcement of PMMA

Modification of Silica with PMMA Via Ultrasonic Irradiation and Its Application for Reinforcement of Polyacrylates

On The Silica/Pmma Nanocomposites

Thermal Degradation and Flammability of Nanocomposites Composed of Silica Cross-Linked to Poly(Methyl Methacrylate)

Preparation and Properties Investigation of Pmma/Silica Composites Derived from Silicic Acid

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma

Toughening PMMA with modified nano-SiO2 particles

Effect of MSU-J and Organic Modification on Mechanical and Thermal Properties of PMMA Hybrid Material

ENHANCED MECHANICAL PROPERTIES OF POLYPROPYLENE/SILICA NANOCOMPOSITES WITH SURFACE MODIFICATION OF NANO-SILICA VIA IN SITU COPOLYMERIZATION OF METHYL METHACRYLATE AND BUTYL ACRYLATE

Organic modification of mesoporous SBA-15 and its effect on mechanical properties of PMMA hybrid materials

Modified Silicon Nitride Nanopowder Coating and Its Influence on the Dynamic Mechanical Property of Polymethyl Methacrylate Nanocomposite

Preparation and Application of Silica Nano-particles

Preparation of PMMA/Silica Nanocomposites by MMA Polymerization in the Presence of Silica Crosslinking Agent

Modified nano-silica by two kinds of coupling agents influences the mechanical properties of resin base

[Effect of Nano ZrO2 on Flexural Strength and Surface Hardness of Polymethylmethacrylate].

Facile Synthesis of Poly(methyl methacrylate) Silica Nanocomposite Monolith by In Situ Free Radical Polymerization of Methyl Methacrylate in the Presence of Functionalized Silica Nanoparticles

Preparation of Pmma/Sio2 Composite Particles Via Emulsion Polymerization

Silica Hybrid Particles with Nanometre Polymer Shells and Their Influence on the Toughening of Polypropylene.

Towards Transparent PMMA/SiO2 Nanocomposites with Promising Scratch‐resistance by Manipulation of SiO2 Aggregation Followed by in Situ Polymerization

The Surface Modification of Nanosilica, Preparation of Nanosilica/acrylic Core‐shell Composite Latex, and Its Application in Toughening PVC Matrix

Silica silanization graft-strengthening bone cement poly(methyl methacrylate): process and dynamic mechanical properties