Abstract:Porous silicon (PSi) has developed for many applications such as gas and humidity sensors. Various methods are available to fabricate PSi, and electrochemical anodization is common due to low cost and easy use. Current density, etching/anodization time, type of etching solution, and electrode distance are the parameters determining resulting pores. The substrate used n-type silicon wafer with (111)-orientation and resistivity of 1.5-4.5 Ω.cm with a size of 1.5×1 cm 2 . The cleaning process of the samples employed the RCA cleaning procedure. Conductive contacts required for the electrochemical anodization were aluminum on the samples. The electrodes were the Si sample acting as anode and platinum (Pt) electrode as a cathode. The etching solution using a mixture of HF (40%) and ethanol (99%) with a 1:1 ratio. The electrode distance was 1.5, 2.0, and 2.5 cm. The current density for each electrode distance was 10, 30, and 50 mA/cm 2 with an anodization time of 30 min. SEM and UV-Vis characterizations were applied to obtain surface morphology and reflectance, respectively. For all samples, the reflectance of PSi was lower than the reflectance of the original silicon surface (no pores). This condition indicates that the PSi is suitable as an anti-reflective layer in a solar cell. However, the PSi of reflectance curves has irregular shapes as a function of wavelength for different electrode distance and the current density. The SEM images confirmed that the pores formed on the silicon surface were inhomogeneous. The pore size decreased with the increase of the electrode distance while it increased as the increase of the current density. There was a correlation between pores size and reflectance at specific wavelength numbers.

Heterojunction diodes of soluble conducting polypyrrole with porous silicon

Heterojunctions based on perylene diimide embedded into porous silicon

A Reactor based on P‐N Heterojunction of Polypyrrole and Porous Silicon for Photocatalytic and Electro‐assisted Photocatalytic Performance

Soluble Conducting Polypyrrole Doped with Dbsa-Csa Mixed Acid

Polyacrylic Acid-Doped Polyaniline As P-Type Semiconductor In Schottky-Barrier Electronic Device

Semiconductive Polymer-Doped PEDOT with High Work Function, Conductivity, Reversible Dispersion, and Application in Organic Solar Cells

Facile Synthesis of Hierarchical Nanostructured Polypyrrole and Its Application in the Counter Electrode of Dye-Sensitized Solar Cells

In situ doping polymerization of pyrrole with sulfonic acid as a dopant

Easily accessible conjugated pyrene sulfonates as cathode interfacial materials for polymer solar cells

Interface Chelation Induced by Pyridine‐based Polymer for Efficient and Durable Air‐processed Perovskite Solar Cells

Hydrogen interaction with Pd/SiO2/Si rectifying junction

Soluble conductive polypyrrole synthesized by in situ doping with β‐naphthalene sulphonic acid

Optoelectric Characteristics of Porous Silicon Using A Conducting Polymer

High Performance Nanostructured Silicon-Organic Quasi P-N Junction Solar Cells Via Low-Temperature Deposited Hole and Electron Selective Layer.

Porous Si (111) Fabrication Using Electrochemical Anodization: Effects of Electrode Distance and Current Density

Synthesis and characterization of nanostructured polypyrroles: Morphology-dependent electrochemical responses and chemical deposition of Au nanoparticles

Enhancing the Selectivity and Transparency of the Electron Contact in Silicon Heterojunction Solar Cells by Phosphorus Catalytic Doping

High-Performance Polymer Heterojunction Solar Cells of A Polysilafluorene Derivative

Photovoltaic Device Application of a Hydroquinone-Modified Conductive Polymer and Dual-Functional Molecular Si Surface Passivation Technology

Oxide-Polymer Heterojunction Diodes with a Nanoscopic Phase-Separated Insulating Layer.

Effects of different interface on the stability of hybrid heterojunction solar cells