Abstract:The development of sustainable and environmentally friendly techniques for synthesizing zeolites has attracted much attention, as the use of organic templates and solvents in the hydrothermal synthesis of zeolites is a major obstacle for realizing green and sustainable synthesis ways. Recently, the introduction of the organotemplate-free synthesis method allowed avoiding the use of organic templates, but water as solvent was still required; solvent-free routes on the other hand beared the potential to significantly reduce the amount of polluted wastewater, but organic templates were still present. In this work, we have demonstrated a combined strategy of both organotemplate- and solvent-free conditions to synthesize aluminosilicate zeolites Beta and ZSM-5 (S-Beta and S-ZSM-5), two of the most important zeolites relevant for industry. The samples are thoroughly characterized by XRD patterns, SEM images, N-2 sorption isotherms, UV-Raman spectra, and Si-29 and Al-27 MAS NMR spectra. The results demonstrate that S-Beta and S-ZSM-5 zeolites exhibit almost the same textural parameters (e.g., BET surface area and pore volume) and catalytic performance in cumene cracking and m-xylene isomerization as those of conventional Beta and ZSM-5 zeolites synthesized under hydrothermal conditions (C-Beta and C-ZSM-5). The organotemplate- and solvent-free syntheses of S-Beta and S-ZSM-5 take place at a low-pressure regime and are free of harmful gases as well as give high product yields together with highly efficient consumption of the starting raw materials. These advantages plus the very simple procedures opened the pathway to a highly sustainable zeolite synthesis protocol compared to conventional methods currently employed for C-Beta and C-ZSM-5. Very interestingly, this simple synthesis is a good model for understanding zeolite crystallization. The detail characterizations indicate that the S-Beta crystals are formed from the assembly of zeolite building units, mainly 4MRs, while the SMRs in the framework are just formed in the crystallization of S-ZSM-5, rather than existence in the starting solid mixture. During the crystallization processes, small traces of water play an important role for the hydrolysis and condensation of silica and/or aluminosilicate species.

Cesium-Free Synthesis of Aluminosilicate Rho Zeolite in the Presence of Cationic Polymer

A Cationic Oligomer as an Organic Template for Direct Synthesis of Aluminosilicate ITH Zeolite

Synthesis of Zeolite ZSM-5 Small Particle Aggregates by a Two-Step Method in the Absence of an Organic Template

Direct synthesis of aluminosilicate ITH zeolite in the presence of a small organic template

Synthesis of high alumina ZSM-5 molecular sieve with ethylene diamine as template

Mesoporous Eu-1 Zeolite Synthesized in the Presence of Cationic Polymer

Synthesis of Mesoporous Zeolite Single Crystals with Cheap Porogens

The Templating Effect Of An Easily Available Cationic Polymer With Widely Separated Charge Centers On The Synthesis Of A Hierarchical Zsm-5 Zeolite

Organic-free synthesis of zincoaluminosilicate zeolites from homogeneous gels prepared by a co-precipitation method.

Organic Template-Free Synthesis of ZSM-5/ZSM-11 Co-Crystalline Zeolite

Templated Synthesis of Hierarchically Mesoporous Zeolites from Cationic Polymers and Their Excellent Catalytic Properties

Mesoporous and Al-rich MFI Crystals Assembled with Aligned Nanorods in the Absence of Organic Templates

Highly Mesoporous Single-Crystalline Zeolite Beta Synthesized Using a Nonsurfactant Cationic Polymer As a Dual-Function Template.

Nitrogen- and Halogen-Free Multifunctional Polymer-Directed Fabrication of Aluminum-Rich Hierarchical MFI Zeolites

Aluminous Zsm-48 Zeolite Synthesis Using A Hydroisomerization Intermediate Mimicking Allyltrimethylammonium Chloride As A Structure-Directing Agent

Self-assembly of silicoaluminophosphate nanocrystals in biphasic media with a water-insoluble structure-directing agent

SYNTHESIS OF MESOPOROUS MOLECULAR SIEVES WITH SECONDARY BUILDING UNITS OF β ZEOLITE AT LOW SURFACTANT CONCENTRATION

Sustainable Synthesis Of Zeolites Without Addition Of Both Organotemplates And Solvents

Alcohol-assisted synthesis of high-silica zeolites in the absence of organic structure-directing agents

Direct Synthesis of Aluminosilicate IWR Zeolite from a Strong Interaction Between Zeolite Framework and Organic Template.

Synthesis and CO 2 adsorption performance of high Si/Al ratio DDR zeolites prepared from silica fume