Boosting Lithium-Ion Transport Kinetics by Increasing the Local Lithium-Ion Concentration Gradient in Composite Anodes of Lithium-Ion Batteries
Weiwei Wu,Zhonggui Sun,Qiang He,Xingwang Shi,Xuhui Ge,Jipeng Cheng,Jun Wang,Zhiya Zhang
DOI: https://doi.org/10.1021/acsami.1c01589
2021-03-17
Abstract:Constructing composite electrodes is considered to be a feasible way to realize high-specific-capacity Li-ion batteries. The core–double-shell-structured @TiO<sub>2</sub> would be an ideal design for such batteries, considering that carbon (C) can buffer the volume change and TiO<sub>2</sub> can constrain the structural deformation of Si. Although the electrochemical performance of the shells themselves is relatively clear, the complexity of the multishell heterointerface always results in an ambiguous understanding about the influence of the heterointerface on the electrochemical properties of the core material. In this work, a multilayer film model that can simplify and simultaneously expand the area of the heterointerface is used to study the heterointerfacial behavior. First, a multilayer film TiO<sub>2</sub>/C with different numbers of TiO<sub>2</sub>/C heterointerfaces is studied. It shows that the electrochemical performance is enhanced apparently by increasing the number of TiO<sub>2</sub>/C heterointerfaces. On the one hand, the TiO<sub>2</sub>/C heterointerface exhibits a strong lithium-ion storage capacity. On the other hand, the TiO<sub>2</sub>/C heterointerface appears to effectively promote the local Li-ion concentration gradient and thus boost the Li-ion transport kinetics. Then, TiO<sub>2</sub>/C is combined with Si to construct a composite anode Si/C/TiO<sub>2</sub>. An obvious advantage of TiO<sub>2</sub>/C over single TiO<sub>2</sub> and C is observed. The utilization rate of Si is greatly improved in the first cycle and reaches up to 98% in Si/C/TiO<sub>2</sub>. The results suggest that the electrochemical performance of Si can be greatly manipulated by the heterointerface between the multishells.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c01589?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c01589</a>.Cross-sectional SEM morphologies; XRD patterns and Raman spectra of Group A and Group B samples; cycling performance of pure amorphous TiO<sub>2</sub> and C films at a current density of 0.2 A g<sup>–1</sup>; CV curves obtained at a scanning rate of 0.1 mV s<sup>–1</sup> and the 1st, 2nd, 10th, 100th, and 200th cycle charge–discharge platform curves derived at a current density of 0.2 A g<sup>–1</sup> for TC2, TC3, TC4, and TC5; CV curves at different scanning rates after five cycles and the fitting apparent diffusion coefficients of all the samples; CV curves at different scanning rates after five cycles and the fitting apparent diffusion coefficients of the TiO<sub>2</sub>/Ge and TiO<sub>2</sub>/Si electrodes; CV curves at a scanning rate of 0.1 mV s<sup>–1</sup> and the galvanostatic charge/discharge curves at a current density of 230 mA g<sup>–1</sup> after different cycles for the Si/C, Si/TiO<sub>2</sub> and Si/C/TiO<sub>2</sub> electrodes; EIS spectra before and after 200 cycles for the Si/C, Si/TiO<sub>2</sub>, and Si/C/TiO<sub>2</sub> electrodes; and the corresponding fitting results (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c01589/suppl_file/am1c01589_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology