Magnetic Exchange-Coupled Sm(Co,R)/Cr(R = Al, Si, Ti, Nb, Cu) Series Films for Ultrahigh-Density Longitudinal Recording Media
X Wang,ZY Li,Z Li,CB Cai,ZX Huang,HW Liao,HM Wang,GQ Lin
DOI: https://doi.org/10.1088/0256-307x/20/2/332
2003-01-01
Chinese Physics Letters
Abstract:SmCoR (R=Al,Si,Ti,Nb,Cu)/Cr series films were fabricated as one kind of promising materials for the ultrahigh density longitudinal magnetic recording media. The Sm(Co,Al,Si)/Cr thin films with coercivity up to 2.36 kOe, squareness ratio S near 0.94 and coercive squareness ratio S* about 0.9 were obtained. The Cr interlayer caused magnetic decoupling in Sm(Co,Al,Si)/Cr/Sm(Co,Al,Si) thin films. High coercivity of 3400-3840 Oe and extremely fine grain size of 5-8nm for the magnetic layer were examined. Using different substrate bias among the Sm(Co,Al,Si) (deposited with substrate bias of -150 V)/Sm(Co,Al,Si)(deposited with no substrate bias)/Sm(Co,Al,Si)(deposited with substrate bias of -150 V), the multilayer exhibited high coercivity of 2960 Oe and S* of 0.96. Sm(Co,Al,Si)/Sm(Co,Ti,Cu)/Sm(Co,Nb,Cu) trilayer improved matching between the magnetic layer and the Cr underlayer, and led to increasing in-plane anisotropy, high coercivity of 3280 Oe and S* of 0.92. Lattice matching of SmCoR {1121} and Cr {110}, etc. were found under various conditions. The microstructures of these four kinds of medium were also examined. The results suggest that it is possible to produce Sm(Co,Al,Si,Ti,Nb,Cu) multi-layer media with the combined magnetic properties required for the ultrahigh density magnetic recording.