Abstract:Mesoporous carbons (MC) with controlled pore structure were synthesized using hydrolyzed water glass (sodium silicate) as hard template precursor. The mixture of carbon precursor (resorcinol-formaldehyde) sol and silica sol followed by Sol-Gel process generated a polymer/silica dual hydrogels. After ambient drying, carbonization and HF etching, mesoporous carbons with developed mesoporous structure were obtained. The hydrolysis conditions of water glass including hydrolysis temperature and hydrolysis time, and the weight ratio of RF polymer to silica were studied respectively to investigate their effects on the mesoporous structure. The microstructures of the mesoporous carbons were characterized by N-2 adsorption, SEM and TEM observations. It was found that as-prepared mesoporous carbons displayed disordered mesoporous channels which replicated from the initial colloidal silica networks. The average mesopore size could be precisely adjusted in the range from 6 nm to 12 nm by tuning the hydrolysis time and hydrolysis temperature, while the total porosity could be controlled by changing the weight ratio of polymer precursor to silica. Furthermore, with the assistant of suspension polymerization and spray drying technologies, spherical mesoporous carbons with millimetre and micrometer-sized particles were drying technologies, spherical mesoporous carbons with millimetre and micrometer-sized particles were produced, respectively. The present work provides a low-cost approach for deliberately controlling the mesoporous structure and spherical morphology to mesoporous carbons that can be extended to many different applications.

Preparation of Carbon Micro-Spheres by Hydrothermal Treatment of Methylcellulose Sol

Preparation of Micrometer-Sized Mesoporous Silica Spheres Assisted by Methyl Cellulose

Preparation and characterization of the poplar micro-nano cellulose sustainable carbon spheres

A Green, Rapid, Scalable and Versatile Hydrothermal Strategy to Fabricate Monodisperse Carbon Spheres with Tunable Micrometer Size and Hierarchical Porosity

Preparation of hundred-micron carbon spheres using solvent extraction in a simple microchannel device

Unveiling the Mechanism of Methylcellulose-Templated Synthesis of Al2O3 Microspheres with Organic Solvents As Swelling Agents in Microchannel

Hydrothermal synthesis of carbon microspheres from sucrose with citric acid as a catalyst: physicochemical and structural properties

Opal Promotes Hydrothermal Carbonization of Hydroxypropyl Methyl Cellulose and Formation of Carbon Nanospheres.

Preparation of cerium dioxide microspheres by internal gelation with cerium citrate as precursor

Facile and Novel Hydrothermal Preparation of Functionalised Carbon Microspheres from Glucose by Using Graphene Sheets As A Substrate

Synthesis Of Us Microspheres By A Hydrothermal Microemulsion Method

Hydrothermal Synthesis of Carbon Nanospheres

Facile Preparation, Structural Control and Spheroidization of Mesoporous Carbons Using Hydrolyzed Water Glass As a Template

Preparation of silica microspheres with a broad pore size distribution and their use as the support for a coated cellulose derivative chiral stationary phase.

Decoupled temperature and pressure hydrothermal synthesis of carbon sub-micron spheres from cellulose

Treatment of Discarded Oil in Supercritical Carbon Dioxide for Preparation of Carbon Microspheres

Synthesis and Properties of Carbon Microspheres from Waste Office Paper

Carbon Microspheres Prepared by High Internal Phase Emulsion Polymerization

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

Effect of Carbon Powder on ZrC ZrO2 Microspheres Prepared by Internal Gelation Process

Hydrothermal carbonization of size-controlled carbon microspheres from waste disposable towel with correlation analyze