Degradability And Biocompatibility Of Mesoporous Silica-Based Xerogel

Li Xiao-Sheng,Liu Chang-Sheng,Hong Hua,Dai Cheng-Long,Wu Wen-Jing

DOI: https://doi.org/10.3321/j.issn:1001-4861.2008.12.002

2008-01-01

Chinese journal of inorganic chemistry

Abstract:The mesoporous silica-based xerogel had been synthesized using improved sol-gel method. The thermal effect, crystalline state, structure and morphology characters of xerogel were measured by DTA-TG, XRD, FITR, SEM, TEM and N-2 adsorption-desorption analysis. The degradation characterization and the cellular behavior were investigated by degradation test in simulated body fluid (SBF) and cultivation of cells, respectively. The results indicate that the synthesized xerogel was mesoporous material. The mean diameter of pores and the largest specific surface area of the xerogel were 3 nm and 901 m(2).g(-1), respectively. The low-temperature treated xerogel degraded entirely within 42 days, and degradation simulating curves was in accordance with one-order dynamics reactive equation. The xerogels degradation velocity was controlled at a relative low ratio, and degradation manner transformed into steady linearity character by sintering processes at high temperature, as well as adding calcium and phosphate ingredients into silica-based xeroel. The xerogel promoted the differentiation and conglomeration of C2C12 cells (C3H mice muscle cells), which revealed good biocompatibility of the material.