Abstract:Directionally solidified TiAl microstructures were investigated and it was found that there is competitive growth between the stable phase (β) and metastable phase (α) near the peritectic reaction L+β→α in Ti–Al binary system. The phase selection phenomena of Ti–Al system containing (44–50)at.% Al were theoretically studied based on the criterion of the highest interface temperature and with solidification interface response function model of single-phase alloys. Firstly, according to a thermodynamic model of Ti–Al binary system, a part of the phase diagram with the Al content of (44–50)at.% and above 1740K was calculated. The peritectic reaction temperature is 1763K, and the peritectic composition is Ti–47.3at.% Al. The solidus and liquidus of α and β were described as polynomials. Using these polynomials, Co, Tm, me and ke were determined. Suppose that the solidification of α and β phases conforms to the solidification theory of single phase, the interface temperatures were calculated. For Ti–47at.% Al, when temperature gradient (G) is 10 000K/m, the critical growth rate of α phase from planar to columnar is about 3.6×10−6mm/s. The critical growth rate linearly increases with increasing temperature gradient. With the same computational program, the interface temperatures of α and β phases with Al content from 44 to 50at.% were calculated. Comparing the interface temperatures of α and β phases, and assuming the phase with the higher interface temperature to grow preferentially from the melt, the phase-selection map with the reference frame of the melt composition and the ratio of temperature gradient to growth velocity (G/V) was constructed. The theoretical results are in good agreement with experimental results.

Competition Growth of Α and Β Phases in Ti-50 At.%al Peritectic Alloy During the Rapid Solidification by Laser Melting Technique

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Primary Dendrite Growth Kinetics and Rapid Solidification Mechanism of Highly Undercooled Ti-Al Alloys

Formation Mechanism of B2 Phase and Micro-Mechanical Property of Rapidly Solidified Ti-Al-Nb Alloy

Combined Effects of High Undercooling and Large Cooling Rate on the Microstructure Evolution and Hardening Mechanism of Rapidly Solidified Ti-Al Alloys

Microstructural Evolution of Rapidly Solidified Ti–Al Peritectic Alloy

Directional Growth of Metastable Phase Γ in Laser-Remelted Ti–Al

A Triple Comparative Study of Primary Dendrite Growth and Peritectic Solidification Mechanism for Undercooled Liquid Fe59ti41 Alloy

In-situ investigation of / transformation in -solidifying -TiAl alloys at different cooling rates

Phase transformation mechanism and mechanical properties of Ti-45Al-8Nb alloy prepared by directed laser deposition

Microstructure selection during the directionally peritectic solidification of Ti–Al binary system

Crystal Orientation, Crystallographic Texture and Phase Evolution in the Ti–45Al–2Cr–5Nb Alloy Processed by Selective Laser Melting

In-situ investigation of β/α transformation in β-solidifying γ-TiAl alloys at different cooling rates

Primary Phase Growth and Microstructure Evolution of Rapidly Solidifying Ternary Ti-12Al-8V Alloy

Phase Selection and Microstructural Formation of Rapidly Directionally Solidified Peritectic Fe–Ni Alloys by Laser Surface Remelting

Microstructure Evolution in Directionally Solidified Ti–(50, 52)at%al Alloys

Directional Solidification and Microstructure Selection for Ti-Al Peritectic Alloy

Understanding the solute segregation and redistribution behavior in rapidly solidified binary Ti- X alloys fabricated through non-equilibrium laser processing

Phase and its morphologies of Ti-45%Al alloy directionally solidified at different growth rates

Microstructure Evolution and Performance of Laser-Remelted Ti-6Al-4V Alloy

Preparation of Metastable Phase Materials: Nucleation and Growth Kinetics Considerations