Hot Deformation Behaviors of AZ91 Magnesium Alloy: Constitutive Equation, Ann-Based Prediction, Processing Map and Microstructure Evolution
Dongxiao Wang,Qiangqiang Zhu,Zhenxiong Wei,Baosen Lin,Yi Jing,Yuan Shi,R. D. K. Misra,Jian-Ping Li
DOI: https://doi.org/10.2139/ssrn.3973896
2021-01-01
SSRN Electronic Journal
Abstract:The behavior of hot deformation in an AZ91 magnesium alloy was studied using Arrhenius model and Back-Propagation Artificial Neural Network (BP-ANN) approaches. The hot compression tests of AZ91 alloy were performed on MMS-300 simulator at deformation temperatures and strain rates in the range of 473 K- 623 K and 0.001 s-1- 1 s-1, respectively. The results show that the BP-ANN model has higher accuracy than Arrhenius model and the correlation coefficient is as high as 0.99341. The processing map is divided into three parts: machinable area (A), instability area (INS) (B) and dynamic strain ageing area (DSA) (C and D). The instability mode of area B, C and D gradually changes from cracks to holes with the increase of temperature or the decrease of strain rate. The stable hot-deformation conditions with peak efficiency of power dissipation were concentrated in the range of 523 K, 0.01 s-1, 573 K, 0.01 s-1, 623 K, 0.001-1 s-1, respectively. With the increase of temperature, the deformation mechanism changed from twinning to dynamic recrystallization (DRX), which is a discontinuous dynamic recrystallization (DDRX). Due to dynamic recrystallization, <0001> // CD texture intensity increased with the increase of temperature, and then decreased.